Resin Technology Group TIGA 202-EX High Performance, Fast Cure Adhesive

Category	Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer	Resin Technology Group
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Resin Technology Group TIGA 202-EX High Performance, Fast Cure Adhesive.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Mix ratio 2 to 1 by volume.TIGA 202-EX is a two-part epoxy adhesive offering outstanding shear tensile and peel adhesion. TIGA 202-EX offers a 20 minute pot life and good hardness development within 1 hour of mixing. TIGA 202-EX is a toughened epoxy exhibiting rugged chemical and environmental resistance and durability. TIGA 202-EX is an excellent general purpose adhesive providing exceptional bond strength to a wide variety of substrates, PVC, FRP, Polyacrylic, Steel, and many more.Applications: TIGA 202-EX is excellent for general purpose high speed industrial assembly, electronic applications, component attachment to boards, housing assembly and potting.Information provided by Resin Technology Group.

Physical Properties	Metric	English	Comments
Specific Gravity	1.12 g/cc	1.12 g/cc	Of resin
	1.13 g/cc	1.13 g/cc	Of hardener
Viscosity	60000 cP @Temperature 25.0 °C	60000 cP @Temperature 77.0 °F	Mixed

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	45 - 55	45 - 55	Cured 2 hours at 25°C
	75 - 85	75 - 85	Cured 24 hours at 25°C
	75 - 85	75 - 85
Shear Strength	>= 27.6 MPa	>= 4000 psi	2 hours, 65°C

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	120 °C	248 °F
Minimum Service Temperature, Air	-60.0 °C	-76.0 °F

Processing Properties	Metric	English	Comments
Cure Time	30.0 min @Temperature 65.0 °C	0.500 hour @Temperature 149 °F
	720 - 1200 min @Temperature 25.0 °C	12.0 - 20.0 hour @Temperature 77.0 °F
Pot Life	20 - 30 min	20 - 30 min	Small Mass(15gr.)

Descriptive Properties	Value	Comments
Color	Off-white/Opaque