Ravago Manufacturing Americas Hylex® P1025L Polycarbonate, High Flow, Mold Release
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant |
| Manufacturer | Ravago Manufacturing Americas, LLC |
| Trade Name | Hylex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hylex® P1025L Polycarbonate, High Flow, Mold Release.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Ravago
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | 24-Hr Immersion; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 25 g/10 min @Load 1.20 kg, Temperature 300 °C |
25 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 80 | 80 | ASTM D785 |
| Tensile Strength | 68.9 MPa | 10000 psi | ASTM D638 |
| Elongation at Break | 115 % | 115 % | ASTM D638 |
| Flexural Strength | 91.0 MPa | 13200 psi | ASTM D790 |
| Flexural Modulus | 2.31 GPa | 335 ksi | ASTM D790 |
| Izod Impact, Notched | 6.41 J/cm @Thickness 3.17 mm |
12.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | ASTM D648 |
| Vicat Softening Point | 154 °C | 310 °F | ASTM D1525 |
| Flammability, UL94 | V-2 @Thickness 1.50 mm |
V-2 @Thickness 0.0591 in |
|
| V-2 @Thickness 3.00 mm |
V-2 @Thickness 0.118 in |
||
| V-0 @Thickness 6.00 mm |
V-0 @Thickness 0.236 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.585 | 1.585 | ASTM D542 |
| Haze | 0.50 - 0.80 % @Thickness 3.17 mm |
0.50 - 0.80 % @Thickness 0.125 in |
ASTM D1003 |
| Transmission, Visible | 89 - 91 % @Thickness 3.17 mm |
89 - 91 % @Thickness 0.125 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 4.00e+16 ohm-cm | 4.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 16.1 kV/mm @Thickness 3.17 mm |
410 kV/in @Thickness 0.125 in |
in Air; ASTM D149 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Rigid Extrusion 87560 Polyvinyl Chloride, Rigid (PVC, Rigid)
- MV Labs PD600 PdI2 Palladium(II) iodide
- PolyMirae Moplen EP340G Sheet and Thermoforming Grade Polypropylene
- Chase Plastics CP Pryme® N300STL (DAM) Nylon 6 (Utility Grade), Super Toughened, Internally Lubricated
- Domo 2300L Polypropylene Copolymer
- Chosun Refractories CTL ASP-B Monolithic Refractories for Ladle and Tundish
- Esstech X-865-0000 Adhesive Monomer PMDM, C22H22O12
- Chosun Refractories CSN-A116 Plate Brick
- Arkema Group Pebax® 4033 SN 01 Polyether Block Amide (PEBA) (Conditioned)
Copyright © lookpolymers.com All Rights Reserved