Ravago Manufacturing Americas Hybrid B2025IU Polycarbonate + PBT Alloy

Category	Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer	Ravago Manufacturing Americas, LLC
Trade Name	Hybrid
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Ravago Manufacturing Americas Hybrid B2025IU Polycarbonate + PBT Alloy.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Entec's proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT, and PPO/PPE resin families.Information provided by Ravago.

Physical Properties	Metric	English	Comments
Density	1.17 g/cc	0.0423 lb/in³	ASTM D792
Melt Flow	25 g/10 min @Load 5.00 kg, Temperature 260 °C	25 g/10 min @Load 11.0 lb, Temperature 500 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	51.7 MPa	7500 psi	ASTM D638
Flexural Yield Strength	72.4 MPa	10500 psi	ASTM D790
Flexural Modulus	1.86 GPa	270 ksi	ASTM D790
Izod Impact, Notched	7.47 J/cm	14.0 ft-lb/in	73°F, 0.125 in; ASTM D256
	4.81 J/cm @Temperature -50.0 °C	9.00 ft-lb/in @Temperature -58.0 °F	0.125 in; ASTM D256
	5.34 J/cm @Temperature -40.0 °C	10.0 ft-lb/in @Temperature -40.0 °F	0.125 in; ASTM D256
	6.14 J/cm @Temperature -30.0 °C	11.5 ft-lb/in @Temperature -22.0 °F	0.125 in; ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	88.9 °C	192 °F	Unannealed; ASTM D648

Processing Properties	Metric	English
Rear Barrel Temperature	243 - 266 °C	470 - 510 °F
Middle Barrel Temperature	249 - 271 °C	480 - 520 °F
Front Barrel Temperature	254 - 277 °C	490 - 530 °F
Nozzle Temperature	254 - 271 °C	490 - 520 °F
Mold Temperature	65.6 - 87.8 °C	150 - 190 °F
Drying Temperature	110 °C	230 °F
Dry Time	4 - 6 hour	4 - 6 hour
Shot Size	50 - 80 %	50 - 80 %
Screw Speed	50 - 80 rpm	50 - 80 rpm

Descriptive Properties	Value	Comments
Injection Rate	Moderate