Raschig Group RALUPOL® 8605 UP Polyester

Category Polymer , Thermoset , Polyester, TS , Thermoset Polyester Glass Filled BMC
Manufacturer Raschig Group
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Raschig Group RALUPOL® 8605 UP Polyester.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Glass fiber reinforced polyester molding compound. Resistant to hydrolysis. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS).Processing: Injection moldingInformation provided by Raschig Group
Physical Properties Metric English Comments
Specific Gravity 1.90 - 2.10 g/cc
1.90 - 2.10 g/cc
ISO 1183
Apparent Bulk Density 0.700 - 0.950 g/cc
0.0253 - 0.0343 lb/in³
ISO 60
Water Absorption <= 0.300 %

@Temperature 23.0 °C,
Time 86400 sec
<= 0.300 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.00300 - 0.00400 cm/cm
0.00300 - 0.00400 in/in
Compression; ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength 70.0 - 100 MPa
10200 - 14500 psi
Compression; ISO 527
Modulus of Elasticity 6.00 - 8.00 GPa
870 - 1160 ksi
Compression; ISO 527
Flexural Strength 120 - 140 MPa
17400 - 20300 psi
Compression; ISO 178
Flexural Modulus 15.0 - 20.0 GPa
2180 - 2900 ksi
Compression; ISO 178
Compressive Strength 150 - 200 MPa
21800 - 29000 psi
ISO 604
Charpy Impact Unnotched 1.00 - 1.50 J/cm²
4.76 - 7.14 ft-lb/in²
Compression; ISO 179/1eU
Charpy Impact, Notched 0.350 - 0.500 J/cm²
1.67 - 2.38 ft-lb/in²
Compression; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 10.0 - 20.0 µm/m-°C

@Temperature 50.0 - 100 °C
5.56 - 11.1 µin/in-°F

@Temperature 122 - 212 °F
ISO 11359-2
Thermal Conductivity 0.900 - 1.10 W/m-K
6.25 - 7.63 BTU-in/hr-ft²-°F
ASTM E1461
Maximum Service Temperature, Air 170 °C

@Time 7.20e+7 sec
338 °F

@Time 20000 hour
IEC 60216/T1
210 °C

@Time <=180000 sec
410 °F

@Time <=50.0 hour
IEC 60216/T1
Deflection Temperature at 8.0 MPa >= 200 °C
>= 392 °F
ISO 75-C
Flammability, UL94 V-0

@Thickness 0.750 mm
V-0

@Thickness 0.0295 in
Shrinkage <= 0.100 %

@Temperature 110 °C,
Time 605000 sec
<= 0.100 %

@Temperature 230 °F,
Time 168 hour
Post shrinkage; ISO 2577
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 - 1.00e+15 ohm-cm
1.00e+14 - 1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+13 - 1.00e+14 ohm
1.00e+13 - 1.00e+14 ohm
IEC 60093
Dielectric Constant 4.00 - 5.00

@Frequency 1.00e+6 Hz
4.00 - 5.00

@Frequency 1.00e+6 Hz
IEC 60250
5.00 - 6.00

@Frequency 100 Hz
5.00 - 6.00

@Frequency 100 Hz
IEC 60250
Dielectric Strength 25.0 - 35.0 kV/mm
635 - 889 kV/in
IEC 60243-1
Dissipation Factor 0.0100 - 0.0300

@Frequency 100 Hz
0.0100 - 0.0300

@Frequency 100 Hz
IEC 60250
0.0100 - 0.0300

@Frequency 1.00e+6 Hz
0.0100 - 0.0300

@Frequency 1.00e+6 Hz
IEC 60250
Arc Resistance 180 - 240 sec
180 - 240 sec
ASTM D495
Comparative Tracking Index 600 V
600 V
IEC 60112
Processing Properties Metric English Comments
Shelf Life 6.00 Month

@Temperature 15.0 - 25.0 °C
6.00 Month

@Temperature 59.0 - 77.0 °F
Descriptive Properties Value Comments
Glow wire flammability test 960/1
IEC 60695 2-12
Glow wire ignitability test 875/1
IEC 60695 2-13
Water Absorption <20 mg
24 hr, 23°C; ISO 62