Radici Radilon® A 38 (dry) Nylon 66

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced
Manufacturer	Radici Group Plastics
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Radici Radilon® A 38 (dry) Nylon 66.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Radilon® A is a range of polyamide 66 (PA66) products obtained through the polymerization of hexamethylendiamine and adipic acid, and used for injection, extrusion and blow-molding.Information provided by Radici group.

Physical Properties	Metric	English
Specific Gravity	1.14 g/cc	1.14 g/cc
Water Absorption	8.4 %	8.4 %
Moisture Absorption at Equilibrium	2.1 %	2.1 %

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	95.0 MPa	13800 psi
Elongation at Break	>= 50 %	>= 50 %	Nominal
Elongation at Yield	4.0 %	4.0 %
Tensile Modulus	3.26 GPa	473 ksi
Charpy Impact Unnotched	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F
Charpy Impact, Notched	0.500 J/cm² @Temperature -30.0 °C	2.38 ft-lb/in² @Temperature -22.0 °F
	0.800 J/cm² @Temperature 23.0 °C	3.81 ft-lb/in² @Temperature 73.4 °F

Thermal Properties	Metric	English	Comments
Melting Point	260 °C	500 °F
Deflection Temperature at 0.46 MPa (66 psi)	195 °C	383 °F
Deflection Temperature at 1.8 MPa (264 psi)	80.0 °C	176 °F
Vicat Softening Point	240 °C @Load 5.10 kg	464 °F @Load 11.2 lb	50°C/h
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+11 ohm-cm	>= 1.00e+11 ohm-cm