Qualchem Danamid FGFHUV-30 Polyamide 6, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Qualchem Zrt. |
| Trade Name | Danamid |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Qualchem Danamid FGFHUV-30 Polyamide 6, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Reinforced with glass fiber. Heat and UV stabilized, for long-lasting use at 120-140°C, resistant to artificial light.Information provided by Qualchem Zrt.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | DIN 53479 |
| Filler Content | 28 - 32 % | 28 - 32 % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 105 | 105 | ASTM D785 |
| Tensile Strength at Break | 150 MPa | 21800 psi | 50 mm/min; ISO 527-1,2 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527-1,2 |
| Tensile Modulus | 9.00 GPa | 1310 ksi | ISO 527-1,2 |
| Flexural Strength | 200 MPa | 29000 psi | 10mm/min; DIN 53452 |
| Flexural Modulus | 7.50 GPa | 1090 ksi | DIN 53452 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
ISO 180 |
| Izod Impact, Unnotched (ISO) | 60.0 kJ/m² | 28.6 ft-lb/in² | ISO 180 |
| 50.0 kJ/m² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
ISO 180 | |
| Charpy Impact Unnotched | 2.50 J/cm² @Temperature -20.0 °C |
11.9 ft-lb/in² @Temperature -4.00 °F |
DIN 53453 |
| 3.00 J/cm² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.700 J/cm² @Temperature -20.0 °C |
3.33 ft-lb/in² @Temperature -4.00 °F |
DIN 53453 |
| 0.800 J/cm² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 4.00 mm |
HB @Thickness 0.157 in |
MSZ 10383 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DIN 53482 |
| Comparative Tracking Index | 550 V | 550 V | IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Moisture Content | 2.0 - 2.2 % | 2.0 - 2.2 % | DIN 53714 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP LUBRICOMP DFL36E PC (Europe-Africa-Middle East)
- Shandong Dongyue Shenzhou New Material Co CHF090 Perfluorosulfonic Acid Ion-Exchange Resin (PFSA)
- Samsung Cheil Industries Infino® XI-4208 PA, Glass Filled
- Solvay SIPOMER® COPS-I Sodium 1-Allyloxy-2-Hydroxypropane Sulfonate
- Zeon Chemicals Hydrin® H-55 Epichlorohydrin Homopolymer
- Polyram PlusTek RA303G33 Nylon 66 for Injection Molding, 33% Glass Fiber Reinforced, Heat Stabilized, Hydrolysis Resistant
- Eastman Eastar DN004 PCTG Copolyester
- Asahi Kasei Thermylene® P6-30FG-0877A 30% Glass Fiber Reinforced, UV Stabilized
- Trelleborg AEM Syntac® 450 Syntactic Foam
Copyright © lookpolymers.com All Rights Reserved