Qualchem Danamid FGF-20 Polyamide 6, 20% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Qualchem Zrt. |
| Trade Name | Danamid |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Qualchem Danamid FGF-20 Polyamide 6, 20% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Reinforced with glass fiber.Information provided by Qualchem Zrt.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | DIN 53479 |
| Filler Content | 18 - 22 % | 18 - 22 % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | >= 110 MPa | >= 16000 psi | 50 mm/min; ISO 527-1,2 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527-1,2 |
| Tensile Modulus | 5.70 GPa | 827 ksi | ISO 527-1,2 |
| Flexural Strength | 200 MPa | 29000 psi | 10mm/min; DIN 53452 |
| Charpy Impact Unnotched | >= 2.00 J/cm² @Temperature 23.0 °C |
>= 9.52 ft-lb/in² @Temperature 73.4 °F |
DIN 53453 |
| Charpy Impact, Notched | >= 0.500 J/cm² @Temperature 23.0 °C |
>= 2.38 ft-lb/in² @Temperature 73.4 °F |
DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 4.00 mm |
HB @Thickness 0.157 in |
MSZ 10383 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DIN 53482 |
| Comparative Tracking Index | 550 V | 550 V | IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Moisture Content | 2.0 - 2.2 % | 2.0 - 2.2 % | DIN 53714 |
Users viewing this material also viewed the following:
- PolyOne Syncure™ V0044G RoHS Natural Polyethylene, Crosslinked (XLPE)
- Nye Lubricants UniFlor 8612 (849) (UF) Synthetic Oil
- Lehmann & Voss LUVOCOM® 80-0837-1 Polyacetal-copolymer, with PTFE, lubricant modified
- LG Chemical LUPOY GP2300 PC+GF30%, Heat Resistance
- Momentive Performance Materials Siloprenâ„¢ Electro 242-0 Electrically Insulating Liquid Silicone Rubber
- Huntsman IROGRAN® A 80 H 4698 Polyester-Based TPU-Injection Molding Grade
- Techmer ES HiFill® PBT GF40 40% Glass Filled
- SABIC Innovative Plastics LNP THERMOCOMP ZF0049 PPE+PS
- SABIC Innovative Plastics NORYL N1150 PPE+PS (Europe-Africa-Middle East)
- Polyram RamSter PF300G8 PBT, 40% Glass Fiber
Copyright © lookpolymers.com All Rights Reserved