Schott Glass 8240 Alkaline Earth Aluminosilicate Glass
| Category | Ceramic , Glass |
| Manufacturer | Schott North America |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Schott Glass 8240 Alkaline Earth Aluminosilicate Glass.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Alkaline earth aluminosilicate glass for high temperature application in electrical engineering, for sealing to molybdenum, free from alkali, blue colored, defined absorption Bulb and exhaust tube for halogen lamps for automotive, household, and general lighting The heavy metal content for the elements lead, cadmium, mercury, and hexavalent chromium is below 100 ppmInformation provided by SCHOTT AG.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.67 g/cc @Temperature 25.0 °C |
0.0965 lb/in³ @Temperature 77.0 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Elasticity | 83.0 GPa | 12000 ksi | |
| Poissons Ratio | 0.23 | 0.23 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 4.70 µm/m-°C @Temperature 20.0 - 300 °C |
2.61 µin/in-°F @Temperature 68.0 - 572 °F |
ISO 7991 |
| Thermal Conductivity | 1.10 W/m-K @Temperature 90.0 °C |
7.63 BTU-in/hr-ft²-°F @Temperature 194 °F |
|
| Transformation Temperature, Tg | 790 °C | 1450 °F | ISO 7884-8 |
| Softening Point | 1005 °C | 1841 °F | Viscosity 10<sup>7.6</sup> dPa s; ISO 7884-3 |
| Working Point | 1305 °C | 2381 °F | Viscosity 10<sup>4</sup> dPa s; ISO 7884-2 |
| Annealing Point | 795 °C | 1460 °F | Viscosity 10<sup>13</sup> dPa s; ISO 7884-4 |
| Strain Point | 750 °C | 1380 °F | Viscosity 10<sup>14.5</sup> dPa s; ISO 7884-7 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.546 @Wavelength 587.6 nm |
1.546 @Wavelength 587.6 nm |
|
| UV Transmittance | <= 72 % @Thickness 1.00 mm, Wavelength 330 nm |
<= 72 % @Thickness 0.0394 in, Wavelength 330 nm |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Alkalis | <= 0.030 % | <= 0.030 % | Total Alkali Oxide |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+11 ohm-cm @Temperature 350 °C |
1.00e+11 ohm-cm @Temperature 662 °F |
|
| 1.00e+13 ohm-cm @Temperature 250 °C |
1.00e+13 ohm-cm @Temperature 482 °F |
||
| Dielectric Constant | 6.6 @Frequency 1.00e+6 Hz, Temperature 25.0 °C |
6.6 @Frequency 1.00e+6 Hz, Temperature 77.0 °F |
|
| Dielectric Loss Index | 0.0015 @Frequency 1.00e+6 Hz, Temperature 25.0 °C |
0.0015 @Frequency 1.00e+6 Hz, Temperature 77.0 °F |
| Chemical Properties | Metric | English | Comments |
|---|---|---|---|
| Acid Class, SR | 2 | 2 | DIN 12116 |
| Alkali Class, AR | 2 | 2 | ISO 695 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Hydrolytic Resistance | Class HGB 1 | ISO 719 |
| Stress-optical Coefficient K (10-6mm2N-1) | 2.7 | DIN 52314 |
| tk100(°C) | 630 | DIN 52326 |
Users viewing this material also viewed the following:
- Polymer Resources PC-FD3 Polycarbonate, FDA-compliant Feedstocks, High Flow, Gamma Resistant
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 60 PHR N990 (MT) Filler
- Fainplast Compounds RH 208 Rigid PVC, Antishock Extrusion
- Schott N-F2 Glass
- SABIC Innovative Plastics Valox® 7062HP PBT (Europe-Africa-Middle East)
- Aclo Accucomp ABS ABS810L Medium Impact Grade
- Barlog Plastics KEBAPEAK XF1730 PEEK, 30% glass fiber reinforced
- Carpenter Speed Star® High Speed Steel (Red-Hard) (AISI M2)
Copyright © lookpolymers.com All Rights Reserved