Premix Thermoplastics PRE-ELEC® CP 1318 (discontinued **)

Category	Polymer , Thermoplastic , Polyolefin
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Premix Thermoplastics PRE-ELEC® CP 1318 (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

PRE-ELEC CP 1318 is a conductive thermoplastic compound based on a polyolefin copolymer. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC CP 1318 has excellent mechanical properties and is easy to extrude or injection mould.Typical applications include flexible extruded products like hoses for vacuum cleaners, profiles for seals etc. PRE-ELEC CP 1318 is also suitable for injection molded parts. Test Specimen - 4.0 mm thick, 10.0 mm wide molded rod.Information provided by Premix Thermoplastics Inc.

Physical Properties	Metric	English	Comments
Density	1.10 g/cc	0.0397 lb/in³
Melt Flow	1.0 g/10 min @Load 5.00 kg, Temperature 190 °C	1.0 g/10 min @Load 11.0 lb, Temperature 374 °F	ISO 1133
High Load Melt Index	26 g/10 min @Load 21.6 kg, Temperature 190 °C	26 g/10 min @Load 47.6 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	94	94	ISO 868
Hardness, Shore D	46	46	ISO 868
Tensile Strength, Yield	19.0 MPa	2760 psi	ISO 527
Elongation at Break	500 %	500 %	ISO 527
Izod Impact, Notched	NB @Thickness 4.00 mm, Temperature 23.0 °C	NB @Thickness 0.157 in, Temperature 73.4 °F	ISO 180
Izod Impact, Unnotched	NB @Thickness 4.00 mm, Temperature 23.0 °C	NB @Thickness 0.157 in, Temperature 73.4 °F	ISO 180

Thermal Properties	Metric	English	Comments
Vicat Softening Point	67.0 °C	153 °F	Rate A; ISO 306/A50

Electrical Properties	Metric	English	Comments
Volume Resistivity	<= 10000 ohm-cm	<= 10000 ohm-cm	ISO D-257
Surface Resistance	<= 1e+05	<= 1e+05	ISO D-257

Processing Properties	Metric	English	Comments
Middle Barrel Temperature	210 °C	410 °F	Zone 1; Cylinder
	220 °C	428 °F	Zone 2; Cylinder
	220 °C	428 °F	Zone 3; Cylinder
	230 °C	446 °F	Zone 6; Cylinder
	230 °C	446 °F	Zone 4; Cylinder
	230 °C	446 °F	Zone 5; Cylinder
Die Temperature	220 °C	428 °F	Zone 3
	230 °C	446 °F	Zone 4
	230 °C	446 °F	Zone 1
	230 °C	446 °F	Zone 2
	230 °C	446 °F	Zone 5
Melt Temperature	180 - 230 °C	356 - 446 °F
Mold Temperature	40.0 - 80.0 °C	104 - 176 °F
Roll Temperature	60.0 °C	140 °F	3rd Roll
	80.0 °C	176 °F	2nd Roll
	90.0 °C	194 °F	1st Roll
Drying Temperature	50.0 - 55.0 °C @Time >=10800 sec	122 - 131 °F @Time >=3.00 hour	If stored for longer than 1 year
Moisture Content	<= 0.15 %	<= 0.15 %	When Produced
Injection Pressure	40.0 - 69.6 MPa	5800 - 10100 psi
Shelf Life	12.0 Month	12.0 Month	Normal Storing Conditions

Descriptive Properties	Value	Comments
Appearance	Granule
Color	Black
Injection Speed	Moderate to Low