Polyram RamTough PZ503 Polycarbonate, Flame Retardant
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamTough PZ503 Polycarbonate, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame retardant polycarbonate for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | DIN 53479 |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | |
| Melt Flow | 12 g/10 min @Load 1.20 kg, Temperature 300 °C |
12 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | ASTM-D638 |
| Elongation at Break | 90 % | 90 % | ASTM-D638 |
| Tensile Modulus | 2.60 GPa | 377 ksi | ASTM-D790 |
| Flexural Strength | 90.0 MPa | 13100 psi | ASTM D790 |
| Flexural Modulus | 7.90 GPa | 1150 ksi | ASTM-D790 |
| Izod Impact, Notched | 1.50 J/cm @Temperature 23.0 °C |
2.81 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | DIN 53461 |
| Flammability, UL94 | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
|
| Glow Wire Test | 960 °C | 1760 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | DIN 53482 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ PPH-20C UV Natural Polypropylene Homopolymer (PP Homopolymer)
- RheTech Products P601-01 Polypropylene Copolymer, Black
- S&E Specialty Polymers GA-1057H1-VW1LF PVC
- Chevron Phillips Marlex® 9506H High Performance Series HDPE Blow Molding Resin (discontinued **)
- LyondellBasell TBAcâ„¢ Solvent, Tertiary butyl acetate
- Techmer ES Luriblend® PP GF20 CC GL2 BK 20% Glass Filled
- Formosa Plastics Formolon® 680 PVC
- Covestro Makrolon® 2656 Polycarbonate
- Arkema Group Orgalloy® P 60AD Nylon (Conditioned)
Copyright © lookpolymers.com All Rights Reserved