Polyram RamTough PZ500 Polycarbonate, Flame Retardant
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamTough PZ500 Polycarbonate, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame retardant polycarbonate for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | DIN 53479 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | |
| Melt Flow | 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | ASTM-D638 |
| Elongation at Break | 95 % | 95 % | ASTM-D638 |
| Tensile Modulus | 2.40 GPa | 348 ksi | ASTM-D790 |
| Izod Impact, Notched | 2.50 J/cm @Temperature 23.0 °C |
4.68 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | DIN 53461 |
| Flammability, UL94 | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
|
| Glow Wire Test | 850 °C | 1560 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | DIN 53482 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | DIN 53482 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- Potters Industries Q-Cel® 7019 Hollow Engineered Glass Microspheres
- Palm Labs Adhesives Turbo Fuse Series 130 (100 Viscosity) Rapid Bonding Adhesive
- Polykemi AB SCANAMID 66 A53^ F43 Nylon 66, Glass Fiber Reinforced, Modified
- Qualchem Danamid FCF-20 Polyamide 6, 20% Carbon Fiber
- 3M Dyneon™ Fluorel™ FG-5630Q Fluoroelastomer VF2 + HFP Dipolymer (discontinued **)
- International Mold Steel Daido DRM2 Matrix High-Speed Steel
- Karina 10/70-IE White Color Concentrate MBU
- Sylvin Technologies 9960-65 Natural PVC Molding Compound
- SABIC Innovative Plastics LNP Thermotuf VFM53 PA 66 (Asia Pacific)
- Braskem Idealis 500 High Molecular Weight Polyethylene Powder
Copyright © lookpolymers.com All Rights Reserved