Polyram RamTal PMH2003 Polyacetal Homopolymer for Injection Molding
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamTal PMH2003 Polyacetal Homopolymer for Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
General purpose polyacetal homopolymer for injection molding applications, MFI 3.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.018 - 0.022 cm/cm | 0.018 - 0.022 in/in | ISO 2577 |
| Melt Flow | 2.8 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.8 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 70.0 MPa | 10200 psi | ISO 527 |
| Elongation at Break | 55 % | 55 % | ISO 527 |
| Tensile Modulus | 3.20 GPa | 464 ksi | ISO 527 |
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 163 °C | 325 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
Users viewing this material also viewed the following:
- Polykemi AB POLYelast TPE HJ752 Thermoplastic Elastomer, PP/Elastomer, Mineral Reinforced
- LyondellBasell Plexar® PX3243 Extrudable Tie-Layer Resin, Anhydride Modified LLDPE
- Menzolit Menzolit® HPC 1200 Unsaturated Polyester UP
- A. Schulman POLYBATCH™ Dark Grey 80431U Concentrate Based In LLDPE
- Covestro Bayfill® 380 Polyurethane Semi-Rigid Foam, Polymeric Catalyst, Open Pour, MDI-based 2-Component Liquid System
- Covestro Makrolon® 2405 MAS048 Polycarbonate
- EMS-Grivory Grivory® GVL-6H black 9915 PA*-GF60
- 3D Systems Accura® 25 Plastic for SLA® Systems
- BASF Lupranate® 278 Isocyanate
- Lanxess Pocan® B 3215 000000 PBT, 10% Glass Fiber
Copyright © lookpolymers.com All Rights Reserved