- Polyram RamTal PM3007G2 Polyacetal for Injection Molding, 10% Glass Fiber Reinforced
Polyram RamTal PM3007G2 Polyacetal for Injection Molding, 10% Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 10% Glass Fiber Reinforced |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamTal PM3007G2 Polyacetal for Injection Molding, 10% Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
10% Glass fiber reinforced polyacetal for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 0.20 % | 0.20 % | ISO 62 |
| Linear Mold Shrinkage | 0.0070 - 0.012 cm/cm | 0.0070 - 0.012 in/in | ISO 2577 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 190 °C |
10 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 70.0 MPa | 10200 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Flexural Strength | 100 MPa | 14500 psi | ISO 178 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 4.50 kJ/m² | 2.14 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | ISO 11357 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | IEC 60250 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 GF 15 FRG 2 LW PA6, 15% glass fibre, flame retardant
- Lehmann & Voss LUVOCOM® 19-8365 Polyamide 46, with carbon fiber and PTFE
- LATI Latigea B01 F1 Bio-Polymer
- SABIC Innovative Plastics LNP LUBRICOMP RX85514 PA 66
- A. Schulman POLYBATCH™ Blue LL40299U/3 Concentrate Based In LLDPE
- ExxonMobil Santoprene® 251-80W232 Thermoplastic Elastomer
- Chosun Refractories CUN-50S Nozzle Brick
- Arkema Group Rilsan® AZM 23 G9 T6LD Nylon 12, 23% Glass Fiber Filled (Dry)
- BASF NEOL® Neolpentylglycol Flakes
Copyright © lookpolymers.com All Rights Reserved