Teknor Apex Beetle® 140 BH Nylon 66, Glass Bead Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Bead Filled |
| Manufacturer | Teknor Apex Company |
| Trade Name | Beetle® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teknor Apex Beetle® 140 BH Nylon 66, Glass Bead Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Processing Method: Injection Molding Forms: PelletsInformation Provided by Teknor Apex
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 |
| Water Absorption | 0.90 % | 0.90 % | 24 hr; ASTM D750 |
| Linear Mold Shrinkage | 0.010 - 0.015 cm/cm | 0.010 - 0.015 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 86.2 MPa | 12500 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 134 MPa | 19500 psi | ASTM D790 |
| Flexural Modulus | 4.72 GPa | 685 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm @Temperature 22.8 °C |
0.800 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 257 °C | 495 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 242 °C | 468 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB @Thickness 0.810 mm |
HB @Thickness 0.0319 in |
|
| Oxygen Index | 27 % | 27 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 15.0 kV/mm @Thickness 3.00 mm |
380 kV/in @Thickness 0.118 in |
ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 241 - 257 °C | 465 - 495 °F | |
| Middle Barrel Temperature | 257 - 271 °C | 495 - 520 °F | |
| Front Barrel Temperature | 263 - 279 °C | 505 - 535 °F | |
| Nozzle Temperature | 263 - 282 °C | 505 - 540 °F | |
| Melt Temperature | 263 - 282 °C | 505 - 540 °F | Processing Temperature |
| Drying Temperature | 79.4 °C | 175 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Suggested Moisture, max | 0.2 | |
| Suggested Regrind, max | 25 |
Users viewing this material also viewed the following:
- MMCC Al/Al2O3 Continuous Fiber Aluminum Matrix Composite
- Ineos N20G-00 Polypropylene Impact Copolymer
- Multibase Multi-Flex® A 9402 MR TPE Thermoplastic Elastomer
- SABIC Innovative Plastics LNP STAT-KON DEP42E PC (Asia Pacific)
- SABIC Innovative Plastics NORYL HM3020H PPE+PS (Asia Pacific)
- Dalau Dalcon 020 Virgin PTFE, Carbon (Anti-Static)
- A. Schulman FORMION™ FI 200 Non-Reinforced, Injection Molding Grade Ionomer / Nylon Alloy
- Trelleborg E850 EPDM Rubber
- DuPont Teijin Films Mylar® 75 OL Polyester Film, 75 Gauge
- BASF DTD Amine
Copyright © lookpolymers.com All Rights Reserved