- Polyram RamSter PF310G6 PBT Alloy, 30% Glass Fiber, UV Stabilized
Polyram RamSter PF310G6 PBT Alloy, 30% Glass Fiber, UV Stabilized
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamSter PF310G6 PBT Alloy, 30% Glass Fiber, UV Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% Glass fiber reinforced PBT alloy, low warp properties, UV stabilized for injection molding.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.50 % | 0.50 % | ISO 62 |
| Linear Mold Shrinkage | 0.0015 - 0.0075 cm/cm | 0.0015 - 0.0075 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 140 MPa | 20300 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 9.10 GPa | 1320 ksi | ISO 527 |
| Flexural Strength | 200 MPa | 29000 psi | ISO 178 |
| Flexural Modulus | 8.80 GPa | 1280 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | ISO 11357 |
| Maximum Service Temperature, Air | 130 °C | 266 °F | Continuous use |
| 200 °C | 392 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.8 | 3.8 | IEC 60250 |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 19-8263 Polyamide 46, with carbon fiber and glass fiber, lubricant modified
- SABIC Innovative Plastics LNP LUBRICOMP SCL36 PA12
- Saint-Gobain Norton® T-100 Virgin Skived PTFE Sheet (0.015" thick)
- Teknor Apex UNIPRENE® 7010-55 Thermoplastic Elastomer
- Thermoseal KLINGERSIL® C-8200 Chemical Resistant Gasketing
- Wingate Alloys Winco XR Special High Strength Alloy Wear Bar
- Wellman Wellamid® 42L-XE-N Nylon 6, Engineering Grade
- Arkema Group KYNAR FLEX® 2950-05 Polyvinylidene Fluoride Copolymer - Extrusion & Molding
- 3M Scotch-Weld™ SI100 Surface Insensitive Instant Adhesive
Copyright © lookpolymers.com All Rights Reserved