Polyram RamOfin PPH308G8 Polypropylene, 40% Glass Fiber
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Glass Fiber Filler |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamOfin PPH308G8 Polypropylene, 40% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
40% glass fiber reinforced, heat stabilized, impact modified polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | DIN 53479 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | |
| Melt Flow | 2.5 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.5 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM-D785 |
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | ASTM-D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM-D638 |
| Flexural Strength | 120 MPa | 17400 psi | ASTM D790 |
| Flexural Modulus | 6.20 GPa | 899 ksi | ASTM-D790 |
| Izod Impact, Notched | 1.70 J/cm @Temperature 23.0 °C |
3.18 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Continuous Use |
| 140 °C | 284 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
Users viewing this material also viewed the following:
- PPT FP150 Fully Sintered Ferrite Powder
- SABIC FI1157 Bimodal High Density Polyethylene for Blown Film
- Abatron 7505-2A/501B Filled Potting Compound (discontinued **)
- PolyOne Geon™ HC 2155G Polyvinyl Chloride, Flexible (PVC, Flexible)
- Lendell Nolatex® Latex Free Foam
- Skamol Group Skamol M-20 Insulating Mortar
- Fainplast Compounds CKL 80 Flexible PVC, Sheathing Lead Free
- Ascend Performance Materials VYDYNE® R543 Nylon, 43% Glass Reinforced, DAM
- Polyplastics Duracon® HP90X Acetal Co-polymer (POM), High stiffness, General
Copyright © lookpolymers.com All Rights Reserved