- Polyram RamOfin PPC350M6 Polypropylene, 30% Mineral Filled
Polyram RamOfin PPC350M6 Polypropylene, 30% Mineral Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamOfin PPC350M6 Polypropylene, 30% Mineral Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% Mineral filled, heat stabilized polypropylene for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.80 g/cc | 0.0650 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | ISO 2577 |
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | ISO 527 |
| Elongation at Break | 25 % | 25 % | ISO 527 |
| Tensile Modulus | 3.00 GPa | 435 ksi | ISO 527 |
| Flexural Strength | 40.0 MPa | 5800 psi | ISO 178 |
| Flexural Modulus | 2.30 GPa | 334 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.50 kJ/m² | 2.62 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | ISO 11357 |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Continuous use |
| 120 °C | 248 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ISO 75 |
| Vicat Softening Point | 80.0 °C | 176 °F | ISO 306 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
Users viewing this material also viewed the following:
- DuPont Bynel® 4006 Anhydride-Modified HDPE Adhesive Resin (discontinued **)
- Eastman Neostar FN005 Elastomer
- CP-Polymer-Technik Wellamid® 6000 GV 25 HWCP 25% Glass Fiber Nylon 6, Heat Stabilized, Conditioned
- Akzo Nobel Expancel® 091 DU 80 Dry unexpanded microspheres
- ArcelorMittal 15 High formability steel for drawing, Hot rolled
- BASF Neopolen® P 9230 A 0.04 g/cc Core density; Expanded Polypropylene (Europe)
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 50 PHR N550 (FEF) Filler
- Zeon Chemicals Nipol® 9025 Polyblack Masterbatch
- LyondellBasell Higlass PF062-2 Polypropylene Homopolymer, 20% Glass Fiber
Copyright © lookpolymers.com All Rights Reserved