Polyram RamLloy A001 Nylon 66/Polyethylene Alloy for Injection Molding, Impact Modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Polyethylene (PE) |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamLloy A001 Nylon 66/Polyethylene Alloy for Injection Molding, Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 66/PE Alloy, reduction of water absorption, impact modified, for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 8.0 % | 8.0 % | ISO 62 |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | ISO 2577 |
| Melt Flow | 15 g/10 min @Load 5.00 kg, Temperature 275 °C |
15 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527 |
| Elongation at Break | 50 % | 50 % | ISO 527 |
| Tensile Modulus | 1.65 GPa | 239 ksi | ISO 527 |
| Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
| Flexural Modulus | 1.79 GPa | 260 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.3 @Frequency 1.00e+6 Hz |
3.3 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60250 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® C6200 PC+ABS
- LG Chemical Acrylic Acid
- Techmer ES HiFill® PA6/6 GF45 L BK 45% Glass Filled
- Styron EMERGEâ„¢ 4530-10 Polycarbonate
- A. Schulman POLYTROPE™ TPP 1008-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer
- Lubrizol ESTANE® 5701F1 Ester Based Thermoplastic Polyurethane (European Grade)
- Dow C700-35 Polypropylene Resin
- Dow DOWLEX™ 2045.11 Linear Low Density Polyethylene, Heavy Duty Film Grade
- Dow Corning 3-4170 DIELECTRIC GEL KIT
Copyright © lookpolymers.com All Rights Reserved