Polyram PlusTek PB840 Nylon 6, Impact Modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek PB840 Nylon 6, Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Impact modified polyamide 6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | DIN 53479 |
| Water Absorption | 8.0 % | 8.0 % | DIN 53495 |
| Moisture Absorption at Equilibrium | 2.5 % | 2.5 % | 50%RH; DIN 53714 |
| Linear Mold Shrinkage | 0.012 - 0.016 cm/cm | 0.012 - 0.016 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 114 | 114 | ASTM-D785 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ASTM-D638 |
| Elongation at Break | 50 % | 50 % | ASTM-D638 |
| Flexural Strength | 85.0 MPa | 12300 psi | ASTM D790 |
| Flexural Modulus | 2.20 GPa | 319 ksi | ASTM-D790 |
| Izod Impact, Notched | 2.20 J/cm @Temperature 23.0 °C |
4.12 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 218 °C | 424 °F | |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | Continuous Use |
| 180 °C | 356 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | DIN 53482 |
| Dielectric Constant | 3.5 @Frequency 1e+6 Hz |
3.5 @Frequency 1e+6 Hz |
VDE 0303/4 |
| Dielectric Strength | 100 kV/mm | 2540 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- Nye Lubricants 753MS (NG) Synthetic Oil
- Fiberfil® J-60/30/F Polypropylene Homopolymer, 30% Glass Reinforced, Chemically coupled
- Hardwire 12x-4-12 Low Density Composite
- Karina E 854-35/9-A-ERYB Ivory PVC Compound
- Lavergne VYPET VNT 245 PET - PBT 45% Glass Reinforced Polyester
- Polyplastics Duranex® CN7130 Polybutylene Terephthalate (PBT), Low friction, Low wear, GF filled
- Westlake Epolene® C-18P Coating Grade - Branched Medium Molecular Weight Polyethylene Polymer
- A. Schulman POLYBATCH™ Ivory 9035 Concentrate Based In Polyethylene
- Hexcel® HexForce™ XLS9114 Carbon/Wire Fabric
Copyright © lookpolymers.com All Rights Reserved