Polyram PlusTek PA350M4 Nylon 6.6 for Injection Molding, 20% Mineral Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Mineral Filled |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek PA350M4 Nylon 6.6 for Injection Molding, 20% Mineral Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% Mineral Reinforced Nylon 6.6 for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 2.2 % | 2.2 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 6.6 % | 6.6 % | ISO 62 |
| Linear Mold Shrinkage | 0.0090 - 0.013 cm/cm | 0.0090 - 0.013 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | |
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Flexural Strength | 150 MPa | 21800 psi | ISO 178 |
| Flexural Modulus | 4.00 GPa | 580 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 6.50 kJ/m² | 3.09 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 11357 |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | Continuous use |
| 200 °C | 392 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz |
3.7 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 90.0 kV/mm | 2290 kV/in | IEC 60250 |
Users viewing this material also viewed the following:
- Ineos Nova 2580 General Purpose Crystal Polystyrene (discontinued **)
- Kobe Steel KS100 Commercially Pure Titanium, Annealed
- SABIC Innovative Plastics LNP LUBRICOMP RAL23 PA 66 (Asia Pacific)
- SABIC Innovative Plastics ULTEM 1000P PEI (Asia Pacific)
- Spartech CastAlloy Weatherable Sheet
- Techmer ES Luriblend® PA6/6 LX Nylon 66
- Wellman Wellamid® MRGF3822-BK 38% Mineral/10% Glass Fiber Reinforced Nylon 66, Heat Stabilized
- ExxonMobil EXACT™ 3128 Plastomer for Blown Film Applications
- Unifrax Fiberfrax® Duraset® Flet
Copyright © lookpolymers.com All Rights Reserved