Polyram PlusTek PA324G6 Nylon 6.6, UL-94 V-0 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek PA324G6 Nylon 6.6, UL-94 V-0 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Self extinguishing (UL-94 V-0) 30% glass fiber reinforced polyamide 6.6 for component with high stiffness and dimensional stabilityInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | DIN 53479 |
| Water Absorption | 6.0 % | 6.0 % | DIN 53495 |
| Moisture Absorption at Equilibrium | 1.4 % | 1.4 % | 50%RH; DIN 53714 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM-D785 |
| Tensile Strength, Yield | 135 MPa | 19600 psi | ASTM-D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM-D638 |
| Flexural Strength | 210 MPa | 30500 psi | ASTM D790 |
| Flexural Modulus | 9.50 GPa | 1380 ksi | ASTM-D790 |
| Izod Impact, Notched | 1.00 J/cm @Temperature 23.0 °C |
1.87 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | |
| Maximum Service Temperature, Air | 120 °C | 248 °F | Continuous Use |
| 200 °C | 392 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | DIN 53461 |
| Flammability, UL94 | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | DIN 53482 |
| Dielectric Constant | 3.8 @Frequency 1e+6 Hz |
3.8 @Frequency 1e+6 Hz |
VDE 0303/4 |
| Dielectric Strength | 70.0 kV/mm | 1780 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- BASF Capron® HPN 9315G HS BK-102 Impact Modified, 15% Glass-Filled Nylon 6 (Dry) (discontinued **)
- Lehmann & Voss LUVOCOM® 3-7281/PL/HI/BK Polyamide 6, with PTFE, toughness-modified
- Indium Corp. Indalloy 157 Lead Solder Alloy
- Solvay TECHNYL® A 225F PA66, Conditioned
- SK Chemicals SKYPET® BL8450 Specially Formulated PET Copolymer Resin
- Hexcel® HexPly® ES 84 120°C Curing Epoxy Matrix, Aramid Balanced fabric 175 g/m2
- Master Bond EP42HT-2 Epoxy Adhesive Resists Sterilization
- DuPont Performance Polymers Zytel® 73G50HSLA BK416 Nylon 6 (Unverified Data**)
- BASF Ultraform N 2200 G53 UNC Q600 25% Glass Filled POM
- Mateck Zero Expansion Glass - ZERODUR
Copyright © lookpolymers.com All Rights Reserved