Polyram PlusTek PA301G3 Nylon 6.6, Heat Stabilized, 15% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek PA301G3 Nylon 6.6, Heat Stabilized, 15% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Heat stabilized, 15% glass fiber reinforced polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | DIN 53479 |
| Water Absorption | 7.0 % | 7.0 % | DIN 53495 |
| Moisture Absorption at Equilibrium | 2.2 % | 2.2 % | 50%RH; DIN 53714 |
| Linear Mold Shrinkage | 0.0045 - 0.0055 cm/cm | 0.0045 - 0.0055 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ASTM-D785 |
| Tensile Strength, Yield | 130 MPa | 18900 psi | ASTM-D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM-D638 |
| Flexural Strength | 190 MPa | 27600 psi | ASTM D790 |
| Flexural Modulus | 6.00 GPa | 870 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.600 J/cm @Temperature 23.0 °C |
1.12 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | |
| Maximum Service Temperature, Air | 120 °C | 248 °F | Continuous Use |
| 240 °C | 464 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | DIN 53482 |
| Dielectric Constant | 3.5 @Frequency 1e+6 Hz |
3.5 @Frequency 1e+6 Hz |
VDE 0303/4 |
| Dielectric Strength | 90.0 kV/mm | 2290 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- Quadrant EPP Semitron® ESd 520HR (ASTM Product Data Sheet)
- EG100A-B20 Polyurethane-based Biomedical Elastomer
- MV Labs TM870 Tm2(C2O4)3·6H2O Thulium oxalate hydrate
- BASF Capron® 8203C HS Blend Nylon 6 (Conditioned) (discontinued **)
- Kolon KOPA® KN333HRBL Heat Resistant Nylon 66
- Lanxess Durethan® BKV 35 H2.0 EF 901510 Nylon 6, 35% Glass Fiber
- Haynes 556® alloy, bar, after 8000 hours at 650°C (1200°F)
- Schott F5 Glass
- DSM Arnitel® EM402-L Injection Molding; Coating Grade Copolyester Elastomer (North America) (discontinued **)
- Beijing Evergrow Resources ER-W-40G Polypropylene Super-Fine Filter Material
Copyright © lookpolymers.com All Rights Reserved