Polymer Resources TP-IM1 Polybutylene Terephthalate, Low Temperature Impact Modified

Category	Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Impact Grade
Manufacturer	Polymer Resources, LTD
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polymer Resources TP-IM1 Polybutylene Terephthalate, Low Temperature Impact Modified.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Polybutylene Terephthalate, Low Temperature Impact ModifiedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.

Physical Properties	Metric	English	Comments
Specific Gravity	1.22 g/cc	1.22 g/cc	ASTM D792
Linear Mold Shrinkage	0.023 - 0.027 cm/cm	0.023 - 0.027 in/in	ASTM D955
Melt Flow	2.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 250 °C	2.0 - 8.0 g/10 min @Load 4.76 lb, Temperature 482 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	37.9 MPa	5500 psi	ASTM D638
Tensile Strength, Yield	37.9 MPa	5500 psi	ASTM D638
Flexural Strength	55.8 MPa	8100 psi	ASTM D790
Flexural Modulus	1.78 GPa	258 ksi	ASTM D790
Izod Impact, Notched	7.47 J/cm @Temperature -28.9 °C	14.0 ft-lb/in @Temperature -20.0 °F	ASTM D256
	8.01 J/cm @Temperature 22.8 °C	15.0 ft-lb/in @Temperature 73.0 °F	ASTM D256
Gardner Impact	36.2 J	26.7 ft-lb	ASTM D3029

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	98.9 °C	210 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	48.9 °C	120 °F	ASTM D648
Flammability, UL94	HB @Thickness 1.59 mm	HB @Thickness 0.0626 in
	HB @Thickness 3.17 mm	HB @Thickness 0.125 in

Processing Properties	Metric	English
Rear Barrel Temperature	232 - 249 °C	450 - 480 °F
Middle Barrel Temperature	238 - 254 °C	460 - 490 °F
Front Barrel Temperature	243 - 260 °C	470 - 500 °F
Melt Temperature	232 - 260 °C	450 - 500 °F
Mold Temperature	43.3 - 76.7 °C	110 - 170 °F
Drying Temperature	116 - 121 °C	240 - 250 °F
Dry Time	3.00 - 4.00 hour	3.00 - 4.00 hour

Descriptive Properties	Value	Comments
Vent	0.0005

Users viewing this material also viewed the following: