Gromax BFG30-EN04B2 Nylon 6 36% Glass Filled (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled |
| Manufacturer | Gromax |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gromax BFG30-EN04B2 Nylon 6 36% Glass Filled (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Gromax Enterprises Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ISO 1183 |
| Moisture Absorption | 0.860 % | 0.860 % | ISO 62 |
| Maximum Moisture Content | 0.10 | 0.10 | Karl Fischer |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Temperature 80.0 °C |
0.0030 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Temperature 80.0 °C |
0.0060 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 91 | 91 | [N/mm<sup>2<sup>]; ISO 7619 |
| Tensile Strength | 137 MPa | 19900 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 2.4 % | 2.4 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 7.40 GPa | 1070 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 226 MPa | 32800 psi | 5 mm/min; ISO 178 |
| Flexural Modulus | 8.73 GPa | 1270 ksi | 5 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 7.10 kJ/m² | 3.38 ft-lb/in² | ISO 180-1A |
| Charpy Impact Unnotched | 6.60 J/cm² @Temperature 23.0 °C |
31.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU |
| Charpy Impact, Notched | 0.730 J/cm² @Temperature 23.0 °C |
3.47 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75-1,-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | ISO 294 |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | ISO 294 |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour |
Users viewing this material also viewed the following:
- SABIC P6006 Black High Density Polyethylene for Pipes
- Abatron 2232 A/B Filled Potting Compound (discontinued **)
- Imerys KT Cast Slurryâ„¢ Kaolin
- Samsung Cheil Industries Starex® BF-0370 MABS, Unreinforced Scratch Resistant
- SABIC Innovative Plastics NORYL HNA055 PPE+HIPS (Europe-Africa-Middle East)
- Eurostar Star C BX6088 ABS, 20% Carbon Filled, Injection Molding
- ACC MM928 Condensation Cure 2-Part Molding Rubber
- Arlon R31030R025 0.025" Uncured Silicone Rubber with Fiberglass Substrate
- Bulk Molding Compounds BMC 900 Thermoset Polyester, Soft Flow Encapsulation Grade
- RheTech Products GC15P200-01 15% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, Black
Copyright © lookpolymers.com All Rights Reserved