- Polymer Resources PPX/NY G10 PPO/Nylon 66 Alloy , 10% Glass Reinforced
Polymer Resources PPX/NY G10 PPO/Nylon 66 Alloy , 10% Glass Reinforced
| Category | Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources PPX/NY G10 PPO/Nylon 66 Alloy , 10% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyphenylene Oxide/Nylon 66 Alloy , 10% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.010 cm/cm | 0.0050 - 0.010 in/in | ASTM D955 |
| Melt Flow | 2.0 - 8.0 g/10 min @Load 3.80 kg, Temperature 300 °C |
2.0 - 8.0 g/10 min @Load 8.38 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 86.2 MPa | 12500 psi | ASTM D638 |
| Tensile Strength, Yield | 86.2 MPa | 12500 psi | ASTM D638 |
| Flexural Strength | 141 MPa | 20500 psi | ASTM D790 |
| Flexural Modulus | 3.52 GPa | 510 ksi | ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm @Temperature 22.8 °C |
0.900 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C | 400 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 216 °C | 420 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0626 in |
|
| HB @Thickness 3.17 mm |
HB @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 268 - 302 °C | 515 - 575 °F | |
| Middle Barrel Temperature | 274 - 302 °C | 525 - 575 °F | |
| Front Barrel Temperature | 279 - 302 °C | 535 - 575 °F | |
| Melt Temperature | 279 - 302 °C | 535 - 575 °F | |
| Mold Temperature | 79.4 - 121 °C | 175 - 250 °F | |
| Drying Temperature | 93.3 - 107 °C | 200 - 225 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.001 |
Users viewing this material also viewed the following:
- Polikim KESTLUB® Polyamide 6 + Lubricant
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 1.0 PHR MBT
- Haveg Havaflex T.A.-118 Phenolic, Trowelable Ablative Coating
- SABIC Innovative Plastics NORYL HFG300 PPE+PS (Asia Pacific)
- Polyram PlusTek PA310G8BK10 Nylon 6.6 for injection Molding, 40% Glass Fiber Reinforced, Heat Stabilized
- DuPont Performance Polymers Crastin® CE2055 BK580 Polybutylene Terephthalate (PBT)
- 3M Scotchcal™ 8000LF-13 Graphic Film
- SABIC Innovative Plastics Lexan® HP4NR PC (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved