- Polymer Resources AC-GP2-TFE5 Acetal Copolymer, 5% PTFE
Polymer Resources AC-GP2-TFE5 Acetal Copolymer, 5% PTFE
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, PTFE Filled |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources AC-GP2-TFE5 Acetal Copolymer, 5% PTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.018 - 0.021 cm/cm | 0.018 - 0.021 in/in | ASTM D955 |
| Melt Flow | 6.0 - 12 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.0 - 12 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 51.7 MPa | 7500 psi | ASTM D638 |
| Tensile Strength, Yield | 50.3 MPa | 7300 psi | ASTM D638 |
| Flexural Strength | 89.6 MPa | 13000 psi | ASTM D790 |
| Flexural Modulus | 2.76 GPa | 400 ksi | ASTM D790 |
| Izod Impact, Notched | <= 0.534 J/cm @Temperature 22.8 °C |
<= 1.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Gardner Impact | 22.6 J | 16.7 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 149 °C | 300 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 220 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0626 in |
|
| HB @Thickness 3.17 mm |
HB @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 179 - 191 °C | 355 - 375 °F | |
| Middle Barrel Temperature | 185 - 196 °C | 365 - 385 °F | |
| Front Barrel Temperature | 191 - 202 °C | 375 - 395 °F | |
| Melt Temperature | 199 - 213 °C | 390 - 415 °F | |
| Mold Temperature | 82.2 - 107 °C | 180 - 225 °F | |
| Drying Temperature | 76.7 - 82.2 °C | 170 - 180 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.0005 |
Users viewing this material also viewed the following:
- Quantum PEEK 30% Glass Fiber Filled
- Overview of materials for Polycyclohexylenedimethylene Terephthalate (PCT), 30% Glass Reinforced
- LATI LARIL 13 G/20 20% Glass Fiber Reinforced Polyphenylene Oxide (PPOm) (Unverified Data**)
- Materion Beryllium Copper Alloy 25 Rod and Bar; H (TD04) Temper; over 25.4 to 76 mm (UNS C17200)
- Lucas-Milhaupt AL 716 Aluminum Brazing Filler Metal
- Seals Eastern 5795 Fluorocarbon-Elastomer
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 70A, Non-Black Peroxide Cure
- EMS-Griltech Griltex® D 1564A Heat Stabilized Copolyamide Hotmelt Adhesive (Technical Applications)
- Colorite Polymers CS6023GP Non Lead Wire and Cable Vinyl Compound
- EMS-Grivory Grivory® CA 6 E PA*
Copyright © lookpolymers.com All Rights Reserved