Polykemi AB SCANLON A 5005B PA/ABS-Blend
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend , Nylon |
| Manufacturer | Polykemi AB |
| Trade Name | SCANLON A |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB SCANLON A 5005B PA/ABS-Blend.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | With Flow; ISO 2577 |
| 0.0090 cm/cm | 0.0090 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 7.5 g/10 min @Load 5.00 kg, Temperature 240 °C |
7.5 g/10 min @Load 11.0 lb, Temperature 464 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 64 @Time 15.0 sec |
64 @Time 0.00417 hour |
ASTM D2240 |
| Tensile Strength at Break | <= 40.0 MPa | <= 5800 psi | ISO/R527 |
| Elongation at Break | >= 150 % | >= 150 % | ISO/R527 |
| Flexural Strength | <= 50.0 MPa | <= 7250 psi | ISO 178 |
| Flexural Modulus | 1.40 GPa @Temperature 23.0 °C |
203 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 4.50 J/cm² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 105 °C @Load 5.001 kg |
221 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| 185 °C @Load 1.00 kg |
365 °F @Load 2.21 lb |
50°C/h; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Glow Wire Test | 650 °C @Thickness 2.00 mm |
1200 °F @Thickness 0.0787 in |
IEC 695-2-1 |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hylon® N1000STHLUV2 HF Nylon 6/6 (discontinued **)
- Kraton® D1163 P (SIS) Linear Triblock Copolymer
- Techmer ES Luriblend® PA6/6 AF10 HS L Nylon 66
- ELM® SoyLube® All Purpose Lubricant and Penetrating Oil
- CP-Polymer-Technik Wellamid® 6600/50 GV 15 HWCP 15% Glass Fiber Nylon 66, Impact Modified Until 0°C, Heat Stabilized, Conditioned
- Daelim H&L Plavis G15 Aromatic Polyimide, 15% Graphite Filled, Machined Parts
- Aclo Accutech Polypropylene HP0335T40V Homopolymer Talc Reinforced
- Colorite Polymers 5512 Clear Injection Molding Vinyl Compound
Copyright © lookpolymers.com All Rights Reserved