- Polykemi AB SCANBLEND P AP2060 F30 PBT/ASA, Glass Fiber Reinforced
Polykemi AB SCANBLEND P AP2060 F30 PBT/ASA, Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , ASA Polymer , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + ASA Blend, Glass Fiber Reinforced |
| Manufacturer | Polykemi AB |
| Trade Name | SCANBLEND P |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB SCANBLEND P AP2060 F30 PBT/ASA, Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 |
| Filler Content | 30 % | 30 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | With Flow; ISO 2577 |
| 0.0070 cm/cm | 0.0070 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 23 g/10 min @Load 2.16 kg, Temperature 275 °C |
23 g/10 min @Load 4.76 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 110 MPa | <= 16000 psi | ISO/R527 |
| Elongation at Yield | 2.0 % | 2.0 % | ISO/R527 |
| Flexural Strength | <= 160 MPa | <= 23200 psi | ISO 178 |
| Flexural Modulus | 9.30 GPa @Temperature 23.0 °C |
1350 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Charpy Impact, Notched | 0.800 J/cm² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 148 °C @Load 5.001 kg |
298 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| 215 °C @Load 1.00 kg |
419 °F @Load 2.21 lb |
50°C/h; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Glow Wire Test | 750 °C @Thickness 2.00 mm |
1380 °F @Thickness 0.0787 in |
IEC 695-2-1 |
Users viewing this material also viewed the following:
- PlastiComp Complet® LGF20 - TPU Rigid Thermoplastic Polyurethane, 20% Long Glass Fiber Reinforced
- Lehmann & Voss LUVOCOM® 1850-7942 PBT, with PTFE, lubricant modified
- IRPC Polimaxx Pentfoam 455E Expandable Polystyrene
- A. Schulman POLYBATCH™ Green 3315 Concentrate Based In Polyethylene
- Formosa Plastics Formolene® 5140H Compression Molding Polypropylene
- A. Schulman POLYBATCH™ Bright Pink 50379 Concentrate Based In Polyethylene
- BASF Ultramid® B3EG6 30% Glass Filled PA6 (Conditioned)
- 3M Fluorinert™ FC-43 Electronic Liquid
Copyright © lookpolymers.com All Rights Reserved