- Lord Adhesives Aeroglaze® 9929 Epoxy Primer
Lord Adhesives Aeroglaze® 9929 Epoxy Primer
| Category | Polymer , Thermoset , Epoxy |
| Manufacturer | Lord Adhesives |
| Trade Name | Aeroglaze® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lord Adhesives Aeroglaze® 9929 Epoxy Primer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Aeroglaze® 9929 epoxy primer is designed to be used on properly prepared aluminum and steel surfaces for applications that require protection against corrosion.All information provided by Lord.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in³ | 9929B; ASTM D1475-85 |
| 1.35 g/cc | 0.0488 lb/in³ | Mixed; ASTM D1475-85 | |
| 1.48 g/cc | 0.0535 lb/in³ | 9929A; ASTM D1475-85 | |
| Solids Content | 47.2 % | 47.2 % | 9929A; by volume; ASTM D2369-87 Modified |
| 49.8 % | 49.8 % | Mixed; by volume; ASTM D2369-87 Modified | |
| 58.8 % | 58.8 % | 9929B; by volume; ASTM D2369-87 Modified | |
| 61.7 % | 61.7 % | 9929B; by weight; ASTM D2369-87 Modified | |
| 68.6 % | 68.6 % | Mixed; by weight; ASTM D2369-87 Modified | |
| 69.8 % | 69.8 % | 9929A; by weight; ASTM D2369-87 Modified | |
| Volatile Organic Compounds (VOC) Content | 355 g/l | 355 g/l | 9929B; ASTM D3960-89 |
| 436 g/l | 436 g/l | Mixed; ASTM D3960-89 | |
| 450 g/l | 450 g/l | 9929A; ASTM D3960-89 | |
| Brookfield Viscosity | 390 cP @Temperature 25.0 °C |
390 cP @Temperature 77.0 °F |
9929B; ASTM D2369-87; LVT |
| 735 cP @Temperature 25.0 °C |
735 cP @Temperature 77.0 °F |
Mixed; ASTM D2369-87; LVT | |
| 4800 cP @Temperature 25.0 °C |
4800 cP @Temperature 77.0 °F |
9929A; ASTM D2369-87; LVT | |
| Outgassing - Total Mass Loss | 1.93 % | 1.93 % | ASTM E595-77 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flash Point | 21.1 °C | 70.0 °F | 9929A; Setaflash, Closed Cup; ASTM D3278-82 |
| 29.4 °C | 84.9 °F | 9929B; Setaflash, Closed Cup; ASTM D3278-82 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 - 240 min @Temperature 25.0 °C |
2.00 - 4.00 hour @Temperature 77.0 °F |
1 dry mil; tack free |
| 420 - 600 min @Temperature 25.0 °C |
7.00 - 10.0 hour @Temperature 77.0 °F |
4 dry mils; tack free | |
| Shelf Life | 12.0 Month | 12.0 Month |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Clear Amber | 9929B |
| Yellow | Mixed | |
| Yellow | 9929A | |
| Coating Film Dry Weight (gm/ft²/mil) | 4.81 | |
| Mix Ratio | 3.5:1 | by volume |
| 5.5:1 | by weight |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ PPC-20G Nat Polypropylene Copolymer (PP Copolymer)
- Omnia Plastica PEEK Polyetheretherketone
- Mar-Bal MB2000-10 Thermoset Polyester Composite Molding Compound
- Schwartz Technical Plastics LAMIGAMID® 309 Cast Polyamide 6, Oil Filled, Dry
- Samsung Cheil Industries Starex® SR-0340M High Heat Grade ABS
- Teknor Apex MF 150 NT Polyvinyl Chloride, Flexible Film
- DSM Fibre Intermediates Nyrim® 1500 (Conditioned)
- Eurotec® Tecodur® PB70 GR30 NL IL PBT 30% glass fiber reinforced, impact modified
- DuPont Teijin Films Mylar® RSX Polyester Film, 175 Gauge
- ATI Allegheny Ludlum Stainless Steel Type 201, 40% Cold Work (UNS S20100)
Copyright © lookpolymers.com All Rights Reserved