Polykemi AB SCANBLEND FS7 PC/ASA Blend with Improved Weather Resistance

Category Polymer , Thermoplastic , ASA Polymer , Polycarbonate (PC) , Polycarbonate/ASA Alloy, Unreinforced
Manufacturer Polykemi AB
Trade Name SCANBLEND
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB SCANBLEND FS7 PC/ASA Blend with Improved Weather Resistance.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
With Flow; ISO 2577
0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
Across Flow; ISO 2577
Melt Index of Compound 20 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 20 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break <= 48.0 MPa
<= 6960 psi
ISO/R527
Elongation at Yield 7.0 %
7.0 %
ISO/R527
Flexural Strength <= 82.0 MPa
<= 11900 psi
ISO 178
Flexural Modulus 2.50 GPa

@Temperature 23.0 °C
 363 ksi

@Temperature 73.4 °F
 ISO 178
Charpy Impact, Notched 4.50 J/cm²

@Temperature 23.0 °C
 21.4 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 121 °C
250 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 102 °C
216 °F
120°C/h; ISO 75/1
Vicat Softening Point 123 °C

@Load 5.001 kg
 253 °F

@Load 11.03 lb
 50°C/h; ISO 306
136 °C

@Load 1.00 kg
 277 °F

@Load 2.21 lb
 50°C/h; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in