Asia International Enterprise (Hong Kong) 30G3 Polybutylene terephthalate, 15% Glass Fiber Filled
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled |
| Manufacturer | Asia Int'l Enterprise (Hong Kong) Limited |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asia International Enterprise (Hong Kong) 30G3 Polybutylene terephthalate, 15% Glass Fiber Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Asia International Enterprise (Hong Kong) Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc @Temperature 23.0 °C |
1.41 g/cc @Temperature 73.4 °F |
ASTM D792 |
| Filler Content | 15 % | 15 % | |
| Linear Mold Shrinkage | 0.0050 - 0.012 cm/cm | 0.0050 - 0.012 in/in | ASTM D955 |
| Melt Flow | 25 g/10 min @Load 2.16 kg, Temperature 250 °C |
25 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 98.1 MPa | 14200 psi | 5mm/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | 5mm/min; ASTM D638 |
| Flexural Strength | 147 MPa | 21300 psi | 2.8mm/min; ASTM D790 |
| Flexural Modulus | 4.90 GPa | 711 ksi | 2.8mm/min; ASTM D790 |
| Izod Impact, Notched | 0.588 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
1.10 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 230 - 265 °C | 446 - 509 °F | Cylinder Temperature |
| Mold Temperature | 50.0 - 100 °C | 122 - 212 °F | |
| Drying Temperature | 120 - 140 °C | 248 - 284 °F | |
| Dry Time | 3 - 5 hour | 3 - 5 hour |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® HPM1914 PC Copolymer
- Ferro IP 900 Passivation Glasses (Pb-B-Si-Al; Pb-Si-Al; Si-Pb-Al Silicates)
- Techmer ES Elastoblend® PA6 GF30 IM HS L 30% Glass Filled (Dry)
- Teknor Apex Telcar® TL-2572A Thermoplastic Elastomer
- Clariant Renol PURSP0005 Polyurethane Elastomer, Glass Fiber Reinforced
- 3M 420 Lead Foil Tape
- 3M ScotchPad™ 3750P Tape Pad
- A. Schulman LP642 Narrow Molecular Weight Copolymer, High-Density Polyethylene
- Eastman Tenite Butyrate 465A3720010 Clear, Trsp Cellulose Acetate Butyrate (discontinued **)
- SABIC Innovative Plastics Lexan® FL1000 PC
Copyright © lookpolymers.com All Rights Reserved