Polykemi AB SCANAMID 66 AL220L2M Nylon 66, Impact Modified

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade
Manufacturer Polykemi AB
Trade Name SCANAMID 66
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB SCANAMID 66 AL220L2M Nylon 66, Impact Modified.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.11 g/cc
0.0401 lb/in³
ISO 1183
Linear Mold Shrinkage 0.015 cm/cm
0.015 in/in
With Flow; ISO 2577
0.017 cm/cm
0.017 in/in
Across Flow; ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break <= 75.0 MPa
<= 10900 psi
ISO/R527
Elongation at Break 6.0 %
6.0 %
ISO/R527
Flexural Strength <= 100 MPa
<= 14500 psi
ISO 178
Flexural Modulus 2.50 GPa

@Temperature 23.0 °C
 363 ksi

@Temperature 73.4 °F
 ISO 178
Charpy Impact, Notched 1.00 J/cm²

@Temperature -20.0 °C
 4.76 ft-lb/in²

@Temperature -4.00 °F
 ISO 179
1.65 J/cm²

@Temperature 23.0 °C
 7.85 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 200 °C
392 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
120°C/h; ISO 75/1
Vicat Softening Point 220 °C

@Load 5.001 kg
 428 °F

@Load 11.03 lb
 50°C/h; ISO 306
>= 250 °C

@Load 1.00 kg
 >= 482 °F

@Load 2.21 lb
 50°C/h; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
Glow Wire Test 650 °C

@Thickness 2.00 mm
 1200 °F

@Thickness 0.0787 in
 IEC 695-2-1