Polykemi AB SCANAMID 66 A43^E F14 Nylon 66, Glass Fiber Reinforced, Modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled |
| Manufacturer | Polykemi AB |
| Trade Name | SCANAMID 66 |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB SCANAMID 66 A43^E F14 Nylon 66, Glass Fiber Reinforced, Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ISO 1183 |
| Filler Content | 14 % | 14 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | With Flow; ISO 2577 |
| 0.012 cm/cm | 0.012 in/in | Across Flow; ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 73 @Time 15.0 sec |
73 @Time 0.00417 hour |
ASTM D2240 |
| Tensile Strength at Break | <= 100 MPa | <= 14500 psi | ISO/R527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO/R527 |
| Flexural Strength | <= 155 MPa | <= 22500 psi | ISO 178 |
| Flexural Modulus | 4.20 GPa @Temperature 23.0 °C |
609 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -20.0 °C |
5.71 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| 1.60 J/cm² @Temperature 23.0 °C |
7.61 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | >= 200 °C @Load 5.001 kg |
>= 392 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Glow Wire Test | 650 °C @Thickness 2.00 mm |
1200 °F @Thickness 0.0787 in |
IEC 695-2-1 |
Users viewing this material also viewed the following:
- PolyOne LubriOne™ AT-000/10T Acetal (POM) Copolymer
- Permabond 931 Cyanoacrylate
- Lanxess Durethan® DP A 32 901510 Nylon 66
- Momentive Performance Materials TSE 221-8U Heat Cured Rubber
- Techmer ES HiFill® HDPE TM20 UV BK 20% Talc Filled
- CP-Polymer-Technik Wellamid® 6000 GVS 10/20 HWUVCP 10% Glass Fiber and 20% Glass Sphere Nylon 6, UV Stabilized, Heat Stabilized, Dry
- ExxonMobil Label-Lyte® 95 LBM-301 White Opaque OPP Film for Blow Mold Label Applications
- China Tungsten STG70Cu-25 PM Structural Parts
- Barlog Plastics KEBAFORM C 906 LF POM Copolymer unreinforced, improved wear and friction
Copyright © lookpolymers.com All Rights Reserved