Polykemi AB SCANAMID 66 A12^ F35 Nylon 66, Glass Fiber Reinforced, Modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | Polykemi AB |
| Trade Name | SCANAMID 66 |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB SCANAMID 66 A12^ F35 Nylon 66, Glass Fiber Reinforced, Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Filler Content | 35 % | 35 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | With Flow; ISO 2577 |
| 0.010 cm/cm | 0.010 in/in | Across Flow; ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 195 MPa | <= 28300 psi | ISO/R527 |
| Elongation at Yield | 3.0 % | 3.0 % | ISO/R527 |
| Flexural Strength | <= 255 MPa | <= 37000 psi | ISO 178 |
| Flexural Modulus | 9.60 GPa @Temperature 23.0 °C |
1390 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 1.10 J/cm² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | >= 230 °C @Load 5.001 kg |
>= 446 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Glow Wire Test | 650 °C @Thickness 2.00 mm |
1200 °F @Thickness 0.0787 in |
IEC 695-2-1 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable WJLK61 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Osprey Metals 17-4 PH Stainless Steel Powder (Grade 90% - 16)
- I. Stern 913 High Impact Polystyrene Extrusion Grade
- MarkeTech Zinc Selenide:Tellurium (ZnSe:Te) Scintillator Crystal
- Lanxess Durethan® BKV 215 H2.0 DUS008 901510 Nylon 6, Impact Modified
- CP-Polymer-Technik Wellamid® 6000 MR 409 HWCP Mineral Nylon 6, Heat Stabilized, Conditioned
- Loctite® 577 Coarse Threads Thread Sealant
- Eastman Tenite Butyrate 581A3720016 Clear, Trsp Cellulose Acetate Butyrate (discontinued **)
Copyright © lookpolymers.com All Rights Reserved