Polykemi AB POLYsan FL100 F35 SAN, Glass Fiber-Reinforced

Category Polymer , Thermoplastic , SAN Polymer , Styrene Acrylonitrile (SAN), Molded, Glass Reinforced
Manufacturer Polykemi AB
Trade Name POLYsan
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB POLYsan FL100 F35 SAN, Glass Fiber-Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.31 g/cc
0.0473 lb/in³
ISO 1183
Filler Content 35 %
35 %
±2%; Polykemi
Mechanical Properties Metric English Comments
Tensile Strength at Break <= 105 MPa
<= 15200 psi
ISO/R527
Elongation at Break 6.0 %
6.0 %
ISO/R527
Flexural Strength <= 160 MPa
<= 23200 psi
ISO 178
Flexural Modulus 10.0 GPa

@Temperature 23.0 °C
 1450 ksi

@Temperature 73.4 °F
 ISO 178
Charpy Impact, Notched 0.300 J/cm²

@Temperature 23.0 °C
 1.43 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
0.300 J/cm²

@Temperature -20.0 °C
 1.43 ft-lb/in²

@Temperature -4.00 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 105 °C
221 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 102 °C
216 °F
120°C/h; ISO 75/1
Vicat Softening Point 108 °C

@Load 5.001 kg
 226 °F

@Load 11.03 lb
 50°C/h; ISO 306
115 °C

@Load 1.00 kg
 239 °F

@Load 2.21 lb
 50°C/h; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
Glow Wire Test 650 °C

@Thickness 2.00 mm
 1200 °F

@Thickness 0.0787 in
 IEC 695-2-1