- Polykemi AB POLYfill PPH TS15030 D Polypropylene Homopolymer, Mineral Reinforced
Polykemi AB POLYfill PPH TS15030 D Polypropylene Homopolymer, Mineral Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Talc Filler |
| Manufacturer | Polykemi AB |
| Trade Name | POLYfill |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYfill PPH TS15030 D Polypropylene Homopolymer, Mineral Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 |
| Filler Content | 30 % | 30 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | Across Flow; ISO 2577 |
| 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | With Flow; ISO 2577 | |
| Melt Index of Compound | 15 g/10 min @Load 2.16 kg, Temperature 230 °C |
15 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 35.0 MPa | <= 5080 psi | ISO/R527 |
| Elongation at Break | 25 % | 25 % | ISO/R527 |
| Elongation at Yield | 7.0 % | 7.0 % | ISO/R527 |
| Flexural Strength | <= 50.0 MPa | <= 7250 psi | ISO 178 |
| Flexural Modulus | 2.60 GPa @Temperature 23.0 °C |
377 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 0.200 J/cm² @Temperature -20.0 °C |
0.952 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| 0.400 J/cm² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 83.0 °C @Load 5.001 kg |
181 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| 146 °C @Load 1.00 kg |
295 °F @Load 2.21 lb |
50°C/h; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Glow Wire Test | 750 °C @Thickness 2.00 mm |
1380 °F @Thickness 0.0787 in |
IEC 695-2-1 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P2760 TPE, PP Overmold or Standalone use
- Polygon Polylube™ Fiber Series Epoxy Composite Bearings
- Dielectric Polymers NT-2821 Ultra Tack Tape (discontinued **)
- M. Holland Company LL800 LLDPE (discontinued **)
- H.C. Starck Amperit® 716.066 Chromium Oxide-Titanium Oxide-Silicon Oxide 92-3-5 (Cr2O3-TiO2-SiO2)
- Multibase Multibatch® MP 52206 Anti-split
- Sylvin Technologies 9915-70 Natural PVC Molding Compound
- Arlon 31940C025 0.025" (0.635 mm) Uncured Silicone Rubber on HDPE Carrier
- ChevronTexaco Cleartex® D
Copyright © lookpolymers.com All Rights Reserved