Arkema Group Pebax® MX 1205 SP 01 Polyether Block Amide (PEBA)

Category	Polymer , Thermoplastic , Polyether Block Amide (PEBA)
Manufacturer	Arkema
Trade Name	Pebax®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group Pebax® MX 1205 SP 01 Polyether Block Amide (PEBA).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Polyether block amide PEBAX® MX 1205 SP 01 is a thermoplastic elastomer made of flexible polyether and rigid polyamide. This SP grade has been developed to be heat and UV resistant.Information provided by Arkema Group

Physical Properties	Metric	English	Comments
Density	1.01 g/cc	0.0365 lb/in³	ISO 1183
Water Absorption	1.2 % @Temperature 23.0 °C, Time 86400 sec	1.2 % @Temperature 73.4 °F, Time 24.0 hour	ISO 62
Moisture Absorption at Equilibrium	0.40 % @Temperature 20.0 °C	0.40 % @Temperature 68.0 °F	50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.0040 cm/cm @Thickness 4.00 mm, Time 86400 sec	0.0040 in/in @Thickness 0.157 in, Time 24.0 hour
Linear Mold Shrinkage, Transverse	0.011 cm/cm @Thickness 4.00 mm, Time 86400 sec	0.011 in/in @Thickness 0.157 in, Time 24.0 hour

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	46	46	Instantaneous, Conditioned 15 days at 23°C - 50% RH; ISO 868
	41 @Time 15.0 sec	41 @Time 0.00417 hour	Conditioned 15 days at 23°C - 50% RH; ISO 868
Tensile Strength at Break	42.0 MPa	6090 psi	Conditioned 15 days at 23°C - 50% RH; ASTM D638
Elongation at Break	>= 550 %	>= 550 %	Conditioned 15 days at 23°C - 50% RH; ASTM D638
Flexural Modulus	0.0860 GPa	12.5 ksi	Conditioned 15 days at 23°C - 50% RH; ISO178
Charpy Impact Unnotched	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	ISO 179
Charpy Impact, Notched	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	ISO 179

Thermal Properties	Metric	English	Comments
Melting Point	147 °C	297 °F	ISO 11357
Vicat Softening Point	111 °C @Load 1.02 kg	232 °F @Load 2.25 lb	ISO 306

Processing Properties	Metric	English	Comments
Processing Temperature	220 °C	428 °F	Recommended Extrusion Temperature
	210 - 230 °C	410 - 446 °F	Extrusion Range
Nozzle Temperature	200 - 270 °C	392 - 518 °F
	240 °C	464 °F	Recommended
Mold Temperature	10.0 - 30.0 °C	50.0 - 86.0 °F
Drying Temperature	60.0 - 70.0 °C	140 - 158 °F
Dry Time	4.00 - 6.00 hour	4.00 - 6.00 hour