Polykemi AB POLYfill PP EIP2012 F Polypropylene, Mineral Reinforced, Extrusion grade, Low CLTE

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Talc Filler , Polypropylene, Extrusion Grade
Manufacturer Polykemi AB
Trade Name POLYfill
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Polykemi AB POLYfill PP EIP2012 F Polypropylene, Mineral Reinforced, Extrusion grade, Low CLTE.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 0.980 g/cc
0.0354 lb/in³
ISO 1183
Filler Content 12 %
12 %
±2%; Polykemi
Linear Mold Shrinkage 0.012 - 0.014 cm/cm
0.012 - 0.014 in/in
With Flow; ISO 2577
0.012 - 0.014 cm/cm
0.012 - 0.014 in/in
Across Flow; ISO 2577
Melt Index of Compound 2.0 g/10 min
<br>@Load 2.16 kg,<br> Temperature 230 °C
 2.0 g/10 min
<br>@Load 4.76 lb,<br> Temperature 446 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break <= 20.0 MPa
<= 2900 psi
ISO/R527
Flexural Strength <= 28.0 MPa
<= 4060 psi
ISO 178
Flexural Modulus 1.30 GPa
<br>@Temperature 23.0 °C
 189 ksi
<br>@Temperature 73.4 °F
 ISO 178
Charpy Impact Unnotched NB
<br>@Temperature 23.0 °C
 NB
<br>@Temperature 73.4 °F
 ISO 179
Charpy Impact, Notched 1.30 J/cm²
<br>@Temperature -20.0 °C
 6.19 ft-lb/in²
<br>@Temperature -4.00 °F
 ISO 179
3.00 J/cm²
<br>@Temperature 23.0 °C
 14.3 ft-lb/in²
<br>@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 95.0 °C
203 °F
120°C/h; ISO 75/1
Vicat Softening Point 60.0 °C
<br>@Load 5.001 kg
 140 °F
<br>@Load 11.03 lb
 50°C/h; ISO 306
135 °C
<br>@Load 1.00 kg
 275 °F
<br>@Load 2.21 lb
 50°C/h; ISO 306