- Polykemi AB POLYelast TPE Z406 Thermoplastic Elastomer, SEBS-based
Polykemi AB POLYelast TPE Z406 Thermoplastic Elastomer, SEBS-based
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Polykemi AB |
| Trade Name | POLYelast |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYelast TPE Z406 Thermoplastic Elastomer, SEBS-based.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.014 - 0.020 cm/cm | 0.014 - 0.020 in/in | With Flow; ISO 2577 |
| 0.014 - 0.020 cm/cm | 0.014 - 0.020 in/in | Across Flow; ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 40 @Time 15.0 sec |
40 @Time 0.00417 hour |
Polykemi |
| Tensile Strength at Break | <= 4.50 MPa | <= 653 psi | ISO/R527 |
| Elongation at Break | 750 % | 750 % | ISO/R527 |
| 100% Modulus | 0.00100 GPa | 0.145 ksi | ISO/R527 |
| 300% Modulus | 0.00140 GPa | 0.203 ksi | ISO/R527 |
| Tear Strength | 21.0 kN/m | 120 pli | D624 |
| Compression Set | 16 % @Temperature 23.0 °C, Time 259000 sec |
16 % @Temperature 73.4 °F, Time 72.0 hour |
DIN 53517 |
| 35 % @Temperature 70.0 °C, Time 86400 sec |
35 % @Temperature 158 °F, Time 24.0 hour |
DIN 53517 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 180 - 220 °C | 356 - 428 °F | |
| Mold Temperature | 20.0 - 40.0 °C | 68.0 - 104 °F | |
| Back Pressure | 0.500 - 1.50 MPa | 72.5 - 218 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure () | Low | % of injection pressure |
| Injection Pressure | Low | |
| Injection Speed () | High |
Users viewing this material also viewed the following:
- GrafTech GRAFCELL® FFP-300 SERIES Flow Field Plate Graphite
- Ineos ABS Lustran® SAN Sparkle Highest-Clarity
- LATI Latamid 66 H2 G/25-V0KB1 PA 66, 25% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant
- UBE UMERIT 2500F Metallocene LLDPE
- Covestro Desmopan® DP 9659DU Polyurethane
- Addiplast Addilene J 370 Polypropylene Copolymer
- Carmel Olefins CAPILENE® E 65 F Polypropylene Homopolymer
- Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Double Aged 732°C (1350°F)/8hr/AC to 621°C (1150°F)/8hr/AC
- DuPont Performance Polymers Zytel® 70G25HSLR NC010 Nylon 66 (Unverified Data**)
- Adell HI-10 Impact Modified PBT
Copyright © lookpolymers.com All Rights Reserved