Polykemi AB POLYelast TPE EC90 D50 P05B Thermoplastic Elastomer, PP/EPDM
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polypropylene (PP) |
| Manufacturer | Polykemi AB |
| Trade Name | POLYelast |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYelast TPE EC90 D50 P05B Thermoplastic Elastomer, PP/EPDM.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.012 - 0.015 cm/cm | 0.012 - 0.015 in/in | With Flow; ISO 2577 |
| 0.012 - 0.015 cm/cm | 0.012 - 0.015 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 11 g/10 min @Load 2.16 kg, Temperature 230 °C |
11 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 53 @Time 15.0 sec |
53 @Time 0.00417 hour |
Polykemi |
| Tensile Strength at Break | <= 16.0 MPa | <= 2320 psi | ISO/R527 |
| Elongation at Break | 300 % | 300 % | ISO/R527 |
| Flexural Modulus | 0.650 GPa @Temperature 23.0 °C |
94.3 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 1.50 J/cm² @Temperature -20.0 °C |
7.14 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| 3.00 J/cm² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 87.0 °C | 189 °F | 120°C/h; ISO 75/1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 260 °C | 464 - 500 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Back Pressure | 1.00 - 1.50 MPa | 145 - 218 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure () | 20-40 | % of injection pressure |
| Injection Speed () | Medium |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® HPS1 PC
- 3M Dyneon™ Fluorel™ FT-2481 Fluoroelastomer VF2 + HFP Dipolymer (discontinued **)
- Panipol Oy T Inherently Conductive Polymer
- Solvay Chemicals Ixper® 60C Calcium Peroxide
- Styrolution PS 165 N/L GPPS
- A. Schulman POLYBATCH™ Poly Off-White P90062PF Concentrate Based In Polypropylene
- Eastman PROVISTA Copolymer PETG Copolyester
- DuPont Performance Polymers Zytel® 70G35HSLX BK357 Nylon 66 (Unverified Data**)
- DSM Stanyl® TC502 PA46
- Sax Polymers SAXALEN PPC345G30 Polypropylene Copolymer, 30% Glass Filled
Copyright © lookpolymers.com All Rights Reserved