SABIC Innovative Plastics LNP LUBRICOMP WCP36 PBT (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP WCP36 PBT (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* WCP36 is a compound based on Polybutylene Terephalate resin containing Carbon Fiber, PTFE, Silicone. Added features include; Internally Lubricated, Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00060 cm/cm | 0.00060 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 116 MPa | 16800 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.1 % | 1.1 % | 5 mm/min; ISO 527 |
| 2.1 % | 2.1 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Tensile Modulus | 16.0 GPa | 2320 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 127 MPa | 18400 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 137 MPa | 19900 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 11.5 GPa | 1670 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 22.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
12.2 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C | 388 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10 - 1000 ohm | 10 - 1000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Network Polymers PC-1029
- PolyMirae Moplen HP526N IPP/WQBF Grade Polypropylene
- SABIC Innovative Plastics Lexan® AD4820 PC (Asia Pacific)
- Huntsman IROGRAN® A 85 P 5350 TPU-Polyester
- Greene Tweed CHEMRAZ® E38 Perfluoroelastomer
- H.C. Starck Grade UF 10 Silicon Carbide, SiC
- Indorama StarPet Preformance® N2R PET Resin
- Total HDPE 5502 R3 High Density Polyethylene - Blow Molding
- A. Schulman POLYBATCH™ FTA-50-P Concentrate Based In LLDPE
- EMS-Grivory Grivory® BG-15/2 PA6-GF15
Copyright © lookpolymers.com All Rights Reserved