- PolyOne Stat-Tech™ PS-18CF/000 CM Black Polybutylene Terephthalate (PBT), Carbon Fiber Reinforced (discontinu
PolyOne Stat-Tech™ PS-18CF/000 CM Black Polybutylene Terephthalate (PBT), Carbon Fiber Reinforced (discontinu
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Stat-Tech™ PS-18CF/000 CM Black Polybutylene Terephthalate (PBT), Carbon Fiber Reinforced
(discontinu.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Preliminary Data SheetDescription/Features:Carbon Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | 24 hr. Immersion, -; ASTM D570 |
| Linear Mold Shrinkage | 0.0015 - 0.0020 cm/cm | 0.0015 - 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 117 MPa | 17000 psi | Type 1 - Rigids, Yield, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 12.4 GPa | 1800 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 179 MPa | 26000 psi | ASTM D790 |
| Flexural Modulus | 12.4 GPa | 1800 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.00 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 10 - 1000 ohm-cm | 10 - 1000 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 10 - 1000 ohm | 10 - 1000 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 243 - 277 °C | 470 - 530 °F | Molding |
| Mold Temperature | 82.2 - 110 °C | 180 - 230 °F | |
| Drying Temperature | 82.2 - 110 °C | 180 - 230 °F | 2 hrs |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- FKuR Kunststoff Bio-Flex® S 5630 Compostable PLA Blend
- LG Chemical LUMID GP1200A(W) PA6, Medium Viscosity
- Mid-Mountain Materials HYTEX® 500 Nomex® Industrial Textile
- Solvay Specialty Polymers Amodel® AE-8950 Polyphthalamide (PPA), 50% Glass Fiber
- SABIC Innovative Plastics LNP THERMOCOMP UF009AXP PPA (Europe-Africa-Middle East)
- SABIC Innovative Plastics Noryl GTX GTX979 PPE+PA
- DuPont™ Kapton® 50EN Polyimide Film, 13 Micron Thickness
- Eurotec® Tecolen® CP30 GR20 NL PPCP, 20% glass fiber reinforced, natural, high flow grade
- Ashley Polymers Ashlene® 742L-33G Nylon 6/66, 33% Glass Reinforced
- ExxonMobil Santoprene® 111-80 Thermoplastic Elastomer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved