- Barlog Plastics KEBATRON C2065X3 PPS, cross-linked, 65% glass fiber / mineral reinforced, reduced residual chlorine
Barlog Plastics KEBATRON C2065X3 PPS, cross-linked, 65% glass fiber / mineral reinforced, reduced residual chlorine
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled |
| Manufacturer | Barlog Plastics |
| Trade Name | KEBATRON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Barlog Plastics KEBATRON C2065X3 PPS, cross-linked, 65% glass fiber / mineral reinforced, reduced residual chlorine.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPS-GF/MD 65Information provided by BARLOG plastics GmbH.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.94 g/cc | 0.0701 lb/in³ | ISO 1183 |
| Water Absorption | 0.020 % | 0.020 % | similar to ISO 62 test |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527-1 |
| Elongation at Break | 0.90 % | 0.90 % | ISO 527-1 |
| Tensile Modulus | 20.0 GPa | 2900 ksi | ISO 527-1 |
| Charpy Impact Unnotched | 2.30 J/cm² | 10.9 ft-lb/in² | ISO 179-1eU |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 15.0 µm/m-°C | 8.33 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 285 °C | 545 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | ISO 75-1/-2 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
UL Registered; IEC 60695-11-10 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Resin Type | PPS-GF/MD 65 |
Users viewing this material also viewed the following:
- Nabaltec APYMAG® 40S Magnesium Hydroxide
- PolyOne Geon™ Vinyl Flexible B8501 Polyvinyl Chloride, Flexible (PVC, Flexible)
- LNP Thermocomp® UF-1006 HS Polyphthalamide, Glass Fiber Reinforcement (discontinued **)
- Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 16000 hours
- Sinotek Materials WT80-46/75 Amorphous Graphite Powder
- Eurostar Starflam BFR552Y6 PA6, Mineral/Glass Fiber Filled, Flame Retardant, Injection Molded
- Ashley Polymers Ashlene® 829 Nylon 6
- DuPont Performance Polymers Delrin® 520MP NC010 Acetal Homopolymer (Unverified Data**)
- DuPont Performance Polymers Minlon® 73M40 NC010 Nylon 6 (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved