A. Schulman ComAlloy Voloy® 415 Polyester - PBT, Glass/Mineral Reinforced, Flame Retardant, UL
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass + Mineral Filled |
| Manufacturer | A. Schulman ComAlloy |
| Trade Name | Voloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman ComAlloy Voloy® 415 Polyester - PBT, Glass/Mineral Reinforced, Flame Retardant, UL.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer, ComAlloy International Company.30% Glass/Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.63 g/cc | 0.0589 lb/in³ | |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength, Ultimate | 94.0 MPa | 13600 psi | ASTM D638 |
| Elongation at Break | 3.6 % | 3.6 % | ASTM D638 |
| Flexural Strength | 157 MPa | 22800 psi | ASTM D790 |
| Flexural Modulus | 9.50 GPa | 1380 ksi | ASTM D790 |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.68 J/cm | 6.89 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 210 - 225 °C | 410 - 437 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 219 °C | 426 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 235 - 249 °C | 455 - 480 °F |
Users viewing this material also viewed the following:
- RheTech Products F40-01 40% Glass Fiber/Mineral Co-Reinforced Polypropylene, Chemically Coupled, Black
- PolyOne Nymax™ GF 1200 33 Red 31 A Polyamide 66 (Nylon 66)
- MarkeTech Indium Phosphide Semiconductor Wafer, p-type, Zinc Doped, Czochralski-LEC Grown
- Industrial Laminates/Norplex NP611 Paper Base Laminate
- Lehmann & Voss LUVOCOM® 1-7943 Polyamide 66, with carbon fiber, heat stabilized
- Borealis RF365MO Polypropylene
- Hexcel® HexWeb® HRH-10/OX - 3/16 - 4.0 Aramid Fiber/Phenolic Resin Honeycomb
- Eurostar Staramide BG10HU PA6, 50% Glass Fiber Filled, UV and Heat Stabilized, Injection Molded
- Dow TUFLIN™ HS-7041 NT 7 Linear Low Density Polyethylene Resin
- Dow Corning 3110 SILICONE RUBBER ENCAPSULANT
Copyright © lookpolymers.com All Rights Reserved