LATI Latamid 66 VH G/30 PA 66, 30% Glass Fiber Reinforced, Heat Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer LATI
Trade Name Latamid
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 66 VH G/30 PA 66, 30% Glass Fiber Reinforced, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 66 (PA66) based compound. Heat stabilized. Hydrolysis stabilized. Glycol stabilized. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
Linear Mold Shrinkage, Flow 0.0035 - 0.0065 cm/cm
0.0035 - 0.0065 in/in
Linear Mold Shrinkage, Transverse 0.0075 - 0.0105 cm/cm
0.0075 - 0.0105 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 40.0 MPa

@Temperature 150 °C
 5800 psi

@Temperature 302 °F
65.0 MPa

@Temperature 120 °C
 9430 psi

@Temperature 248 °F
75.0 MPa

@Temperature 90.0 °C
 10900 psi

@Temperature 194 °F
95.0 MPa

@Temperature 60.0 °C
 13800 psi

@Temperature 140 °F
145 MPa

@Temperature 23.0 °C
 21000 psi

@Temperature 73.4 °F
Elongation at Break 2.4 %

@Temperature 23.0 °C
 2.4 %

@Temperature 73.4 °F
4.0 %

@Temperature 60.0 °C
 4.0 %

@Temperature 140 °F
5.0 %

@Temperature 90.0 °C
 5.0 %

@Temperature 194 °F
5.1 %

@Temperature 120 °C
 5.1 %

@Temperature 248 °F
5.4 %

@Temperature 150 °C
 5.4 %

@Temperature 302 °F
Tensile Modulus 2.00 GPa

@Temperature 150 °C
 290 ksi

@Temperature 302 °F
3.50 GPa

@Temperature 120 °C
 508 ksi

@Temperature 248 °F
4.40 GPa

@Temperature 90.0 °C
 638 ksi

@Temperature 194 °F
6.20 GPa

@Temperature 60.0 °C
 899 ksi

@Temperature 140 °F
9.40 GPa

@Temperature 23.0 °C
 1360 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 6.00 J/cm²
28.6 ft-lb/in²
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 130 °C
266 °F
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
Deflection Temperature at 1.8 MPa (264 psi) 245 °C
473 °F
Vicat Softening Point 250 °C

@Load 5.00 kg
 482 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 270 - 290 °C
518 - 554 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa