PolyOne Lubri-Tech™ SY-000/10T-2S Natural Polystyrene (PS), PTFE Lubricated (discontinued **)
| Category | Polymer , Thermoplastic , Polystyrene (PS) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ SY-000/10T-2S Natural Polystyrene (PS), PTFE Lubricated
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:High ImpactPTFE LubricatedInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.11 g/cc | 1.11 g/cc | ASTM D792 |
| Water Absorption | 0.30 % @Thickness 3.17 mm |
0.30 % @Thickness 0.125 in |
24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 8.0 % | 8.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 2.59 GPa | 375 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 31.0 MPa | 4500 psi | ASTM D790 |
| Flexural Modulus | 2.59 GPa | 375 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
2.00 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 210 - 232 °C | 410 - 450 °F | Molding |
| Mold Temperature | 48.9 - 71.1 °C | 120 - 160 °F | |
| Drying Temperature | 48.9 - 65.6 °C | 120 - 150 °F | |
| Dry Time | 2 hour | 2 hour |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ FR PE CONC 1 Polyethylene, Low Density (LDPE)
- Iran Petrochemical (PCC) BL 3VD HH 4765 High Density Polyethylene
- Shin-Etsu Silicones KE-348 Silicone, RTV
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 20 PHR Tricresyl Phosphate
- Covestro Makroblend® UT305 PC/PET Blend
- ExxonMobil Escorene™ UL 7760 Ethylene Vinyl Acetate Copolymer
- ExxonMobil LDPE LD 150BW Low Density Polyethylene Resin
- Dow DOWLEX™ 2035 Linear Low Density Polyethylene, Cast Film Grade
- 3M Scotch® 250 Flatback Masking Tape
- Teknor Apex APEX® 3210-70 Polyvinyl Chloride, Flexible
Copyright © lookpolymers.com All Rights Reserved