PolyOne Lubri-Tech™ PI-10CF/15T Polyetherimide (PEI), Carbon Fiber Reinforced, PTFE Lubricated (discontinued
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ PI-10CF/15T Polyetherimide (PEI), Carbon Fiber Reinforced, PTFE Lubricated
(discontinued.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Carbon Fiber ReinforcedPTFE LubricatedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.398 g/cc | 1.398 g/cc | ASTM D792 |
| Water Absorption | 0.015 % | 0.015 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0025 - 0.0030 cm/cm | 0.0025 - 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 103 MPa | 15000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 6.89 GPa | 1000 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 131 MPa | 19000 psi | ASTM D790 |
| Flexural Modulus | 6.89 GPa | 1000 ksi | ASTM D790 |
| Izod Impact, Notched | 0.908 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.70 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 400 °F | Annealed, 0.125 in bars; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1000 - 1.00e+6 ohm-cm | 1000 - 1.00e+6 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 1000 - 1.00e+6 ohm | 1000 - 1.00e+6 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 343 - 371 °C | 650 - 700 °F | Molding |
| Mold Temperature | 121 - 149 °C | 250 - 300 °F | |
| Drying Temperature | 121 - 149 °C | 250 - 300 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® ML7687 PC (Europe-Africa-Middle East)
- H.C. Starck Amperit® 712.074 Chromium Oxide-Titanium Oxide 75-25 (Cr2O3-TiO2)
- SABIC Innovative Plastics LNP LUBRILOY RA2 PA 66
- A. Schulman POLYFLAM™ E-13030B Reinforced Super Coupled Polypropylene Black
- Hexcel® HexWeb® HRH-78 - 3/16 - 3.0 Commercial Grade Nomex Honeycomb/Phenolic Resin
- Dow Corning LSPBK27 SILICONE MASTERBATCH BLACK
- Dr. D. Mueller Flexiso® DMD FI 14010 00240 Polyester Electrical Insulation
- Diamond Polymers NPP25-1201 TF10 10% Talc Filled Copolymer Polypropylene
- BASF Vinyl Caprolactam
- 3M Scotchkote™ HTX 517 Epoxy HT Lining
Copyright © lookpolymers.com All Rights Reserved