- PolyOne Lubri-Tech™ ATH-000/5T Acetal-Homopolymer, PTFE Lubricated (discontinued **)
PolyOne Lubri-Tech™ ATH-000/5T Acetal-Homopolymer, PTFE Lubricated (discontinued **)
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ ATH-000/5T Acetal-Homopolymer, PTFE Lubricated
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:PTFE LubricatedInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.435 g/cc | 1.435 g/cc | ASTM D792 |
| Water Absorption | 0.010 % @Thickness 3.17 mm |
0.010 % @Thickness 0.125 in |
24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.010 - 0.020 cm/cm | 0.010 - 0.020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 55.2 MPa | 8000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 8.0 % | 8.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 2.83 GPa | 410 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 2.83 GPa | 410 ksi | ASTM D790 |
| Izod Impact, Notched | 0.694 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.30 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 1.00e+17 ohm | 1.00e+17 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- NIZHNEKAMSKNEFTEKHIM PP 4310M (EP1X30F) Propylene and Ethylene Copolymer
- Chevron Phillips Marlex® C579 High density polyethylene (discontinued **)
- Gouda Vuurvast CURAS 90 SPF Moldable Refractory Material
- Solvay Specialty Polymers Tecnoflon® TN 50A Fluoroelastomer
- A. Schulman POLYBATCH™ Green 3012E Concentrate Based In Polyethylene
- ChevronTexaco Meropa® 320
- China Tungsten YT15 Tungsten Carbide for Cutting Tools
- ArcelorMittal HSLA 500 High strength low alloy steel for cold forming, Hot Rolled
Copyright © lookpolymers.com All Rights Reserved