Network Polymers Softflex® 0954
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber |
| Manufacturer | Network Polymers |
| Trade Name | Softflex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Network Polymers Softflex® 0954.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Softflex® Thermoplastic Elastomer AlloyInformation provided by Network Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.032 cm/cm @Thickness 3.17 mm |
0.032 in/in @Thickness 0.125 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.036 cm/cm @Thickness 3.17 mm |
0.036 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 28.9 g/10 min @Load 1.00 kg, Temperature 235 °C |
28.9 g/10 min @Load 2.20 lb, Temperature 455 °F |
Procedure A Condition Q; ASTM D1238 |
| 30.8 g/10 min @Load 5.00 kg, Temperature 200 °C |
30.8 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 64 - 74 | 64 - 74 | 10 second dwell; ASTM D2240 |
| 68 - 78 | 68 - 78 | Instantaneous; ASTM D2240 | |
| Tensile Strength, Yield | 9.535 MPa | 1383 psi | chs 20 in/min; ASTM D412 |
| Elongation at Break | 811 % | 811 % | ASTM D412 |
| 50% Modulus | 0.00257 GPa | 0.373 ksi | ASTM D412 |
| 100% Modulus | 0.00327 GPa | 0.474 ksi | ASTM D412 |
| 300% Modulus | 0.00490 GPa | 0.711 ksi | ASTM D412 |
| Gardner Impact | >= 36.2 J @Temperature -30.0 °C |
>= 26.7 ft-lb @Temperature -22.0 °F |
ASTM D5420 |
| Tear Strength | 45.5 kN/m | 260 pli | ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 0.2382 | 0.2382 | H22 Wheel 1000 g load/1000 cycles; ASTM D3389 |
| Compression Set | 23.9 % | 23.9 % | Method B, 22 hours at 25% deflection and 23°C; ASTM D395 |
| 78.4 % @Temperature 70.0 °C |
78.4 % @Temperature 158 °F |
22 hours at 25% deflection; ASTM D395, Method B, | |
| 96.4 % @Temperature 100 °C |
96.4 % @Temperature 212 °F |
22 hours at 25% deflection; ASTM D395, Method B, | |
| Tensile Set | 7.4 % | 7.4 % |
Users viewing this material also viewed the following:
- Polimeri Europa Europrene® NEOCIS BR 60 Butadiene Rubber
- Hong Kun Group 2,2,6,6-Tetramethyl-piperidine-1-oxyl(TEMPO) Additive
- KaMin KaMin® 611 Kaolin Clay - Waterwashed
- H.C. Starck HPM 1750 Tungsten High Density Composite Sheet
- Shandong Rike Chemical HELIâ„¢ HL-901 PVC Foaming Regulator
- Teknor Apex APEX® 02-A0111A-90NT Polyvinyl Chloride, Flexible
- ExxonMobil Greasrex K-218
- Entec Hyrene® PS-HI 14/2 High Impact Polystyrene
- UBE UBESTA® 3030U Nylon 12 (After Sodium Hydroide for 1000 hours)
- PolyOne Edgetek® PE-30GF/000 WHITE High Density Polyethylene (HDPE), Glass Filled (discontinued **)
Copyright © lookpolymers.com All Rights Reserved