PolyOne Lubri-Tech™ ATH-000/05M Acetal Homopolymer - 5% MoS2  (discontinued **)

Category Polymer , Thermoplastic , Acetal (POM)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Lubri-Tech™ ATH-000/05M Acetal Homopolymer - 5% MoS2  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Data provided by PolyOne.
Physical Properties Metric English Comments
Density 1.44 g/cc
0.0520 lb/in³
ASTM D792
Water Absorption 0.050 %
0.050 %
24 hrs. ASTM D570
Linear Mold Shrinkage 0.020 - 0.025 cm/cm

@Thickness 3.17 mm
 0.020 - 0.025 in/in

@Thickness 0.125 in
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 34.0 MPa
4930 psi
ASTM D638
Elongation at Break 2.0 - 6.0 %
2.0 - 6.0 %
ASTM D638
Tensile Modulus 2.60 GPa
377 ksi
ASTM D638
Flexural Yield Strength 34.0 MPa
4930 psi
ASTM D790
Flexural Modulus 2.60 GPa
377 ksi
ASTM D790
Izod Impact, Notched 0.530 - 0.800 J/cm

@Thickness 6.35 mm
 0.993 - 1.50 ft-lb/in

@Thickness 0.250 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 127 °C
261 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
ASTM D648
Processing Properties Metric English Comments
Melt Temperature 193 - 216 °C
379 - 421 °F
Stock
Mold Temperature 71.0 °C
160 °F
Drying Temperature 71.0 °C
160 °F